LNP™ STAT-KON™ Compound OE008A

Want to keep this datasheet? Save it now in your required format

Description

LNP* STAT-KON* OE008A is a compound based on PPS - Branched resin containing 40% Carbon Fiber. Added feature of this grade is: Electrically Conductive.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electrical Engineering

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.49 g/cm³ Show Supplier Material materials with Density of 1.49 g/cm³	ISO 1183

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	0.7 % Show Supplier Material materials with Elongation of 0.7 %	ISO 527 \| break, 5 mm/min
Flexural modulus	23.0 °C	30.3 GPa Show Supplier Material materials with Flexural modulus of 30.3 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	290 MPa Show Supplier Material materials with Flexural strength of 290 MPa	ISO 178 \| break, 2 mm/min
Impact strength, Izod notched	23.0 °C	6 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 6 kJ/m²	ISO 180/1A \| 80104, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	37 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 37 J/m	ASTM D 256
Impact strength, Izod unnotched	23.0 °C	25 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 25 kJ/m²	ISO 180/1U \| 80104, 23°C
Impact strength, Izod unnotched, ASTM	23.0 °C	480 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 480 J/m	ASTM D 4812 \| 23°C
Tensile strength	23.0 °C	179 MPa Show Supplier Material materials with Tensile strength of 179 MPa	ISO 527 \| break, 5 mm/min

Thermal

Property	Value	Comment
Relative temperature index, electrical	130 °C Show Supplier Material materials with Relative temperature index, electrical of 130 °C	UL 746B
Relative temperature index, mechanical impact	130 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 130 °C	UL 746B
Relative temperature index, mechanical strength	130 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 130 °C	UL 746B
Flammability	UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=102581048- - <br> UL Recognized, 94V-0 Flame Class Rating: 1mm UL 94

Electrical

Property	Temperature	Value	Comment
Sheet resistivity, ROA	23.0 °C	10 - 1000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 10 - 1000 Ω	ASTM D 257

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.1 % Show Supplier Material materials with Shrinkage of 0.1 %	SABIC method \| 3.2 mm
Shrinkage, transverse	23.0 °C	0.6 % Show Supplier Material materials with Shrinkage, transverse of 0.6 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Circuit Protection, Electronic Components
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 120 to 150.0°C Drying Time: 4hrs Melt Temperature: 315 to 320.0°C Front - Zone 3 Temperature: 330 to 345.0°C Middle - Zone 2 Temperature: 320 to 330.0°C Rear - Zone 1 Temperature: 305 to 315.0°C Mold Temperature: 140 to 165.0°C Back Pressure: 0.2 to 0.3MPa Screw Speed: 30 to 60.0rpm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.