General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.24 g/cm³ Show Supplier Material materials with Density of 1.24 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.3 % Show Supplier Material materials with Moisture absorption of 0.3 % | ASTM D 570 | (23°C/50% RH/24 hrs) |
Relative density | 23.0 °C | 1.24 [-] Show Supplier Material materials with Relative density of 1.24 [-] | ASTM D 792 | |
Water absorption | 23.0 °C | 0.4 % Show Supplier Material materials with Water absorption of 0.4 % | ISO 62-1 | (23°C/24hrs) |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.5 GPa Show Supplier Material materials with Elastic modulus of 2.5 GPa | ISO 527 | 1 mm/min | ||
Elongation | 23.0 °C | 5.9 % Show Supplier Material materials with Elongation of 5.9 % | ISO 527 | yield, 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.5 GPa Show Supplier Material materials with Flexural modulus of 2.5 GPa | ISO 178 | 2 mm/min | ||
Flexural strength | 23.0 °C | 115 MPa Show Supplier Material materials with Flexural strength of 115 MPa | ISO 178 | yield, 2 mm/min | ||
Impact strength, Izod notched | 23.0 °C | 6 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 6 kJ/m² | ISO 180/1A | 80*10*4, 23°C | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 69 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 69 J/m | ASTM D 256 | ||
Tensile strength | 23.0 °C | 60 MPa Show Supplier Material materials with Tensile strength of 60 MPa | ISO 527 | break, 50 mm/min | ||
Impact strength, Izod unnotched | ISO 180/1U | unnotched 80*10*4, 23°C |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 6.1E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 6.1E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 6.2E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6.2E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Heat deflection temperature | 170 - 183 °C Show Supplier Material materials with Heat deflection temperature of 170 - 183 °C | ||||
Heat deflection temperature, 0.45 MPa | 183 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 183 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 170 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 170 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 160 °C Show Supplier Material materials with Relative temperature index, electrical of 160 °C | UL 746B | |||
Relative temperature index, mechanical impact | 140 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 140 °C | UL 746B | |||
Relative temperature index, mechanical strength | 160 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 160 °C | UL 746B | |||
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=104116794- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥4.5mm UL 94 <br> UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=104098070- - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 4 V Show Supplier Material materials with Comparative tracking index of 4 V | UL 746A | (UL) {PLC} |
Dissipation factor, 1MHz | 23.0 °C | 6E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 6E-3 [-] | ASTM D 150 |
Dissipation factor, 1kHz | 23.0 °C | 1E-3 [-] Show Supplier Material materials with Dissipation factor, 1kHz of 1E-3 [-] | ASTM D 150 |
Dissipation factor, 50Hz | 23.0 °C | 7E-4 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 7E-4 [-] | ASTM D 150 | 50/60 Hz |
High Amp Arc Ignition | 23.0 °C | 6 mm Show Supplier Material materials with High Amp Arc Ignition of 6 mm | ≥, UL 746A | PLC 3 |
High Volt Arc Track Rate | 23.0 °C | 4 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 4.5 mm Show Supplier Material materials with Hot-Wire Ignition of 4.5 mm | ≥, UL 746A | PLC 1 |
Volume resistivity | 23.0 °C | 3.00E+17 Ω·cm Show Supplier Material materials with Volume resistivity of 3.00E+17 Ω·cm | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Shrinkage | 23.0 °C | 0.4 % Show Supplier Material materials with Shrinkage of 0.4 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Medical Device, Surgical Devices | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120 to 150.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |