Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of friction | 0.46 [-] Show Supplier Material materials with Coefficient of friction of 0.46 [-] | ||
Coefficient of friction, kinetic | 0.46 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.46 [-] | ASTM D 3702 Modified: Manual | |
Coefficient of friction, static | 0.46 [-] Show Supplier Material materials with Coefficient of friction, static of 0.46 [-] | ASTM D 3702 Modified: Manual | |
Density | 23.0 °C | 1.32 g/cm³ Show Supplier Material materials with Density of 1.32 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.1 % Show Supplier Material materials with Moisture absorption of 0.1 % | ASTM D 570 | (23°C/50% RH/24 hrs) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 19.2 GPa Show Supplier Material materials with Elastic modulus of 19.2 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 6.2 % Show Supplier Material materials with Elongation of 6.2 % | ISO 527 | break |
Flexural modulus | 23.0 °C | 17 GPa Show Supplier Material materials with Flexural modulus of 17 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 280 MPa Show Supplier Material materials with Flexural strength of 280 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched | 23.0 °C | 7 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 7 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 53 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 53 J/m | ASTM D 256 |
Impact strength, Izod unnotched | 23.0 °C | 49 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 49 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 801 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 801 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 6 J Show Supplier Material materials with Instrumented Impact, at Peak of 6 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 188 MPa Show Supplier Material materials with Tensile strength of 188 MPa | ISO 527 | break |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.6E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 4.8E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 4.8E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Heat deflection temperature | 212 - 222 °C Show Supplier Material materials with Heat deflection temperature of 212 - 222 °C | ||
Heat deflection temperature, 0.45 MPa | 222 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 222 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 212 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 212 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Document Handling, ATM/Ticket Machine | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 80°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |