NORYL™ Resin NP6100 - Europe

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ NP6100 resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS) designed for high heat resistance with good strength, toughness and robust FR performance. This extrudable grade contains non-brominated, non-chlorinated flame retardant. NORYL NP6100 resin may be an excellent candidate for mining pipe applications as well as low smoke cable channel applications where EN45545 R22 certificate ( European railway standard for small electrical parts) is required.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Relative density	23.0 °C	1.08 [-] Show Supplier Material materials with Relative density of 1.08 [-]	ASTM D 792 \|

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.3 GPa Show Supplier Material materials with Elastic modulus of 2.3 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	4.5 % Show Supplier Material materials with Elongation of 4.5 %	ISO 527 \| yield, 50 mm/min
Flexural modulus	23.0 °C	2.4 GPa Show Supplier Material materials with Flexural modulus of 2.4 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	77 MPa Show Supplier Material materials with Flexural strength of 77 MPa	ISO 178 \| yield, 2 mm/min
Impact strength, Charpy notched	23.0 °C	21 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 21 kJ/m²	ISO 179/1eA \| V-notch Edgew 80104 sp=62mm, -30°C
Impact strength, Izod notched	23.0 °C	15.8 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 15.8 kJ/m²	ISO 180/1A \| notched 80104, -30°C
Impact strength, Izod notched, ASTM	23.0 °C	510 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 510 J/m	ASTM D 256
Tensile strength	23.0 °C	68 MPa Show Supplier Material materials with Tensile strength of 68 MPa	ISO 527 \| yield, 50 mm/min
Impact strength, Charpy unnotched	ISO 179/1eU \| Unnotch Edgew 80104 sp=62mm, -30°C
Impact strength, Izod unnotched	ISO 180/1U \| unnotched 80104, -30°C

Thermal

Property	Value	Comment
Heat deflection temperature	121 - 146 °C Show Supplier Material materials with Heat deflection temperature of 121 - 146 °C
Heat deflection temperature, 0.45 MPa	146 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 146 °C	ISO 75/Bf \| Flatw 80104 sp=64mm
Heat deflection temperature, 1.80 MPa	121 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 121 °C	ASTM D 648 \| 3.2mm, unannealed
Vicat softening temperature	151 °C Show Supplier Material materials with Vicat softening temperature of 151 °C	ISO 306 \| Rate B/50
Flammability	UL Compliant, 94V-1 Flame Class Rating: 1.5mm UL 94 by SABIC-IP <br> Glow Wire Flammability Index 960°C, passes at: 1mm IEC 60695-2-12 <br> Glow Wire Flammability Index 960°C, passes at: 1mm IEC 60695-2-12 <br> Smoke density, DS-max, 25 kW/m2, 1.5 mm: 47- ISO 5659-2

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		10.5 g/10min Show Supplier Material materials with Melt mass-flow rate of 10.5 g/10min	ASTM D 1238 \| 280°C/10.0 kgf
Melt volume-flow rate		11 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 11 cm³/10min	ISO 1133 \| MVR at 280°C/10.0 kg
Shrinkage	23.0 °C	0.5 % Show Supplier Material materials with Shrinkage of 0.5 %	SABIC method \| 3.2 mm
Shrinkage, transverse	23.0 °C	0.5 % Show Supplier Material materials with Shrinkage, transverse of 0.5 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Enclosure/Housing/Cover
Availability	Europe,Asia
Processing methods	Drying Temperature: 90 to 100.0°C Drying Time: 2 to 4.0hrs Drying Time (Cumulative): 6hrs Maximum Moisture Content: 0.02% Melt Temperature: 255 to 275.0°C Rear - Zone 1 Temperature: 235 to 255.0°C Middle - Zone 2 Temperature: 255 to 275.0°C Front - Zone 3 Temperature: 255 to 275.0°C Nozzle Temperature: 255 to 275.0°C Adapter Temperature: 255 to 275.0°C Die Temperature: 255 to 275.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.