General
Property | Temperature | Value | Comment |
---|---|---|---|
Relative density | 23.0 °C | 1.08 [-] Show Supplier Material materials with Relative density of 1.08 [-] | ASTM D 792 | |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.3 GPa Show Supplier Material materials with Elastic modulus of 2.3 GPa | ISO 527 | 1 mm/min | ||
Elongation | 23.0 °C | 4.5 % Show Supplier Material materials with Elongation of 4.5 % | ISO 527 | yield, 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.4 GPa Show Supplier Material materials with Flexural modulus of 2.4 GPa | ISO 178 | 2 mm/min | ||
Flexural strength | 23.0 °C | 100 MPa Show Supplier Material materials with Flexural strength of 100 MPa | ISO 178 | break, 2 mm/min | ||
Impact strength, Charpy notched | 23.0 °C | 21 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 21 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, -30°C | ||
Impact strength, Izod notched | 23.0 °C | 15.8 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 15.8 kJ/m² | ISO 180/1A | notched 80*10*4, -30°C | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 180 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 180 J/m | ASTM D 256 | notched, -30°C | ||
Tensile strength | 23.0 °C | 68 MPa Show Supplier Material materials with Tensile strength of 68 MPa | ISO 527 | yield, 50 mm/min | ||
Impact strength, Charpy unnotched | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C | ||||
Impact strength, Izod unnotched | ISO 180/1U | unnotched 80*10*4, -30°C |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature | 121 - 146 °C Show Supplier Material materials with Heat deflection temperature of 121 - 146 °C | ||
Heat deflection temperature, 0.45 MPa | 146 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 146 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 121 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 121 °C | ASTM D 648 | 3.2mm, unannealed | |
Vicat softening temperature | 151 °C Show Supplier Material materials with Vicat softening temperature of 151 °C | ISO 306 | Rate B/50 | |
Flammability | UL Compliant, 94V-1 Flame Class Rating: 1.5mm UL 94 by SABIC-IP <br> Glow Wire Flammability Index 960°C, passes at: 1mm IEC 60695-2-12 <br> Glow Wire Flammability Index 960°C, passes at: 1mm IEC 60695-2-12 <br> Smoke density, DS-max, 25 kW/m2, 1.5 mm: 47- ISO 5659-2 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 10.5 g/10min Show Supplier Material materials with Melt mass-flow rate of 10.5 g/10min | ASTM D 1238 | 280°C/10.0 kgf | |
Melt volume-flow rate | 11 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 11 cm³/10min | ISO 1133 | MVR at 280°C/10.0 kg | |
Shrinkage | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage of 0.5 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage, transverse of 0.5 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Enclosure/Housing/Cover | |
Availability | Europe,Asia | |
Processing methods | Drying Temperature: 90 to 100.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |