LNP™ STAT-KON™ Compound ME003S - Americas

Want to keep this datasheet? Save it now in your required format

Description

LNP STAT-KON ME003S is a compound based on Polypropylene resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive, Heat Stabilized.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electrical Engineering

Construction

Water Management

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	3 % Show Supplier Material materials with Elongation of 3 %	ASTM D 638 \| break
Flexural modulus	23.0 °C	5.1 GPa Show Supplier Material materials with Flexural modulus of 5.1 GPa	ASTM D 790
Flexural strength	23.0 °C	65 MPa Show Supplier Material materials with Flexural strength of 65 MPa	ASTM D 790
Impact strength, Izod notched	23.0 °C	53 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 53 kJ/m²	ASTM D 256 \| notched, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	16 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 16 J/m	ASTM D 256 \| notched, 23°C
Impact strength, Izod unnotched, ASTM	23.0 °C	320 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 320 J/m	ASTM D 4812 \| 23°C
Tensile strength	23.0 °C	40 MPa Show Supplier Material materials with Tensile strength of 40 MPa	ASTM D 638 \| break

Electrical

Property	Temperature	Value	Comment
Sheet resistivity, ROA	23.0 °C	1000 - 1000000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1000 - 1000000 Ω	ASTM D 257

Technological properties

Property
Application areas	Pump, Oil/Gas, Enclosures
Availability	Asia,Americas
Processing methods	Melt Temperature: 225 to 250.0°C Screw Speed: 30 to 60.0rpm Back Pressure: 0.2 to 0.3MPa Front - Zone 3 Temperature: 240 to 250.0°C Drying Time: 4hrs Rear - Zone 1 Temperature: 195 to 205.0°C Mold Temperature: 30 to 50.0°C Middle - Zone 2 Temperature: 215 to 225.0°C Drying Temperature: 80°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.