LNP LUBRICOMP KFL36 is a compound based on Acetal Copolymer resin containing 30% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electronics

Display Devices

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.75 g/cm³ Show Supplier Material materials with Density of 1.75 g/cm³	ASTM D 792

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	2.3 % Show Supplier Material materials with Elongation of 2.3 %	ISO 527 \| break, 5 mm/min
Flexural modulus	23.0 °C	9.9 GPa Show Supplier Material materials with Flexural modulus of 9.9 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	130 MPa Show Supplier Material materials with Flexural strength of 130 MPa	ISO 178
Impact strength, Izod notched	23.0 °C	5 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m²	ISO 180/1A \| notched 80104, 23°C
Impact strength, Izod unnotched	23.0 °C	25 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 25 kJ/m²	ISO 180/1U \| 80104, 23°C
Tensile strength	23.0 °C	84 MPa Show Supplier Material materials with Tensile strength of 84 MPa	ISO 527 \| break, 5 mm/min

Thermal

Property	Value	Comment
Heat deflection temperature	161 °C Show Supplier Material materials with Heat deflection temperature of 161 °C
Heat deflection temperature, 1.80 MPa	161 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 161 °C	ISO 75/Af \| Flatw 80104 sp=64mm

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.7 % Show Supplier Material materials with Shrinkage of 0.7 %	ASTM D 955 \| 24 hrs

Technological properties

Property
Application areas	Document Handling, Wireless Communications
Availability	Europe,Asia,Americas
Processing methods	Front - Zone 3 Temperature: 210 to 220.0°C Melt Temperature: 200 to 215.0°C Middle - Zone 2 Temperature: 195 to 205.0°C Mold Temperature: 80 to 110.0°C Drying Temperature: 80°C Rear - Zone 1 Temperature: 175 to 190.0°C Screw Speed: 30 to 60.0rpm Back Pressure: 0.2 to 0.3MPa Drying Time: 4hrs
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.