General
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of friction | 0.35 - 0.44 [-] Show Supplier Material materials with Coefficient of friction of 0.35 - 0.44 [-] | ||
Coefficient of friction, kinetic | 0.44 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.44 [-] | ASTM D 3702 Modified: Manual | |
Coefficient of friction, static | 0.35 [-] Show Supplier Material materials with Coefficient of friction, static of 0.35 [-] | ASTM D 3702 Modified: Manual | |
Density | 23.0 °C | 1.7 g/cm³ Show Supplier Material materials with Density of 1.7 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.01 % Show Supplier Material materials with Moisture absorption of 0.01 % | ISO 62 | (23°C / 50% RH) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 12 GPa Show Supplier Material materials with Elastic modulus of 12 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 1.3 % Show Supplier Material materials with Elongation of 1.3 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 11.1 GPa Show Supplier Material materials with Flexural modulus of 11.1 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 180 MPa Show Supplier Material materials with Flexural strength of 180 MPa | ISO 178 |
Impact strength, Izod notched | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 60 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 60 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched | 23.0 °C | 24 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 24 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 416 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 416 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 11 J Show Supplier Material materials with Instrumented Impact, Total Energy of 11 J | ASTM D 3763 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 3 J Show Supplier Material materials with Instrumented Impact, at Peak of 3 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 121 MPa Show Supplier Material materials with Tensile strength of 121 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.4E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.4E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | IEC 60695-2-12 | 0.75 mm | |||
Glow Wire Ignition Temperature | 800 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 800 °C | IEC 60695-2-13 | 0.75 mm | |||
Heat deflection temperature | 257 - 278 °C Show Supplier Material materials with Heat deflection temperature of 257 - 278 °C | ||||
Heat deflection temperature, 0.45 MPa | 278 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 278 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 257 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 257 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 105 °C Show Supplier Material materials with Relative temperature index, electrical of 105 °C | UL 746B | |||
Relative temperature index, mechanical impact | 105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | |||
Relative temperature index, mechanical strength | 105 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C | UL 746B | |||
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101283823- - <br> UL Recognized, 94V-0 Flame Class Rating: 1.5mm UL 94 <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=101282823- - <br> UL Yellow Card Link 3: https://iq.ul.com/ul/cert.aspx?ULID=101344460- - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 4 V Show Supplier Material materials with Comparative tracking index of 4 V | UL 746A | (UL) {PLC} |
High Amp Arc Ignition | 23.0 °C | 0.75 mm Show Supplier Material materials with High Amp Arc Ignition of 0.75 mm | ≥, UL 746A | PLC 2 |
High Volt Arc Track Rate | 23.0 °C | 4 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | ≥, UL 746A | PLC 0 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Document Handling | |
Availability | Americas | |
Processing methods | Drying Temperature: 120 to 150.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |