Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of friction | 0.41 - 0.48 [-] Show Supplier Material materials with Coefficient of friction of 0.41 - 0.48 [-] | ||
Coefficient of friction, kinetic | 0.41 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.41 [-] | ASTM D 3702 Modified: Manual | |
Coefficient of friction, static | 0.48 [-] Show Supplier Material materials with Coefficient of friction, static of 0.48 [-] | ASTM D 3702 Modified: Manual | |
Density | 23.0 °C | 1.37 g/cm³ Show Supplier Material materials with Density of 1.37 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.6 GPa Show Supplier Material materials with Elastic modulus of 2.6 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 5.1 % Show Supplier Material materials with Elongation of 5.1 % | ISO 527 | yield, 5 mm/min |
Flexural modulus | 23.0 °C | 2.4 GPa Show Supplier Material materials with Flexural modulus of 2.4 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 69 MPa Show Supplier Material materials with Flexural strength of 69 MPa | ISO 178 |
Impact strength, Izod notched | 23.0 °C | 14 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 14 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 192 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 192 J/m | ASTM D 256 |
Impact strength, Izod unnotched | 23.0 °C | 105 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 105 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1500 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 1500 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 31 J Show Supplier Material materials with Instrumented Impact, at Peak of 31 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 43 MPa Show Supplier Material materials with Tensile strength of 43 MPa | ISO 527 | yield, 5 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 5.3E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 5.3E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Heat deflection temperature | 135 - 139 °C Show Supplier Material materials with Heat deflection temperature of 135 - 139 °C | ||
Heat deflection temperature, 0.45 MPa | 139 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 139 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 135 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 135 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Surgical Devices | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |