General
Property | Temperature | Value | Comment |
---|---|---|---|
Relative density | 23.0 °C | 1.22 [-] Show Supplier Material materials with Relative density of 1.22 [-] | ASTM D 792 | |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 3.1 GPa Show Supplier Material materials with Elastic modulus of 3.1 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 75 % Show Supplier Material materials with Elongation of 75 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 3.1 GPa Show Supplier Material materials with Flexural modulus of 3.1 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 95 MPa Show Supplier Material materials with Flexural strength of 95 MPa | ISO 178 | yield, 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 11 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Impact strength, Izod notched | 23.0 °C | 20 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 20 kJ/m² | ISO 180/1A | 80*10*3, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 300 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 300 J/m | ASTM D 256 | notched, 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 52 J Show Supplier Material materials with Instrumented Impact, Total Energy of 52 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 56 MPa Show Supplier Material materials with Tensile strength of 56 MPa | ISO 527 | yield, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 8E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 8E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Heat deflection temperature | 81 - 88 °C Show Supplier Material materials with Heat deflection temperature of 81 - 88 °C | ||||
Heat deflection temperature, 0.45 MPa | 88 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 88 °C | ASTM D 648 | 3.2 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 81 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 81 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 60 °C Show Supplier Material materials with Relative temperature index, electrical of 60 °C | UL 746B | |||
Relative temperature index, mechanical impact | 60 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 60 °C | UL 746B | |||
Relative temperature index, mechanical strength | 60 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 60 °C | UL 746B | |||
Flammability | UL Recognized, 94V-1 Flame Class Rating: ≥0.8mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥1mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=100874261- - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Hot-Wire Ignition | 23.0 °C | 3 mm Show Supplier Material materials with Hot-Wire Ignition of 3 mm | ≥, UL 746A | PLC 2 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 11 g/10min Show Supplier Material materials with Melt mass-flow rate of 11 g/10min | ASTM D 1238 | 260°C/2.16 kgf | |
Shrinkage | 23.0 °C | 0.3 % Show Supplier Material materials with Shrinkage of 0.3 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.3 % Show Supplier Material materials with Shrinkage, transverse of 0.3 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Personal Computing | |
Availability | Asia | |
Processing methods | Melt Temperature: 245 to 275.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |