LNP™ THERMOCOMP™ Compound GZ004

Want to keep this datasheet? Save it now in your required format

Description

LNP™ THERMOCOMP™ GZ004 is a compound based on Polysulfone resin containing 20% milled Glass. Added features include: Custom Color GREY

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.35 g/cm³

Show Supplier Material materials with Density of 1.35 g/cm³

ISO 1183

Moisture absorption

23.0 °C

0.1 %

Show Supplier Material materials with Moisture absorption of 0.1 %

ISO 62-4 | (23°C/50% RH/Equilibrium)

Water absorption

23.0 °C

0.5 %

Show Supplier Material materials with Water absorption of 0.5 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3.7 GPa

Show Supplier Material materials with Elastic modulus of 3.7 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

3.6 %

Show Supplier Material materials with Elongation of 3.6 %

ISO 527 | yield, 5 mm/min

Flexural modulus

23.0 °C

3.6 GPa

Show Supplier Material materials with Flexural modulus of 3.6 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

104 MPa

Show Supplier Material materials with Flexural strength of 104 MPa

ISO 178 | break, 2 mm/min

Impact strength, Charpy notched

23.0 °C

7 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 7 kJ/m²

ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C

Impact strength, Izod notched

23.0 °C

5 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m²

ISO 180/1A | 80*10*4, 23°C

Impact strength, Izod unnotched

23.0 °C

40 kJ/m²

Show Supplier Material materials with Impact strength, Izod unnotched of 40 kJ/m²

ISO 180/1U | unnotched 80*10*4

Tensile strength

23.0 °C

57 MPa

Show Supplier Material materials with Tensile strength of 57 MPa

ISO 527 | yield, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

4.9E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 4.9E-5 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

5.2E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5.2E-5 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature

170 - 181 °C

Show Supplier Material materials with Heat deflection temperature of 170 - 181 °C

Heat deflection temperature, 0.45 MPa

181 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 181 °C

ISO 75/Bf | Flatw 80*10*4 sp=64mm

Heat deflection temperature, 1.80 MPa

170 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 170 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Vicat softening temperature

186 °C

Show Supplier Material materials with Vicat softening temperature of 186 °C

ISO 306 | Rate B/50

Flammability

UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101343831- - <br> UL Recognized, 94V-2 Flame Class Rating: 1.5mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: 1.5mm UL 94

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method

Shrinkage, transverse

23.0 °C

0.4 %

Show Supplier Material materials with Shrinkage, transverse of 0.4 %

SABIC method

Technological properties

Property
Application areas

Auto Electrical

Availability

Europe,Asia,Americas

Processing methods

Drying Temperature: 120 to 150.0°C
Drying Time: 4hrs
Maximum Moisture Content: ≤0.05%
Melt Temperature: 360 to 370.0°C
Rear - Zone 1 Temperature: 325 to 340.0°C
Middle - Zone 2 Temperature: 340 to 350.0°C
Front - Zone 3 Temperature: 350 to 360.0°C
Nozzle Temperature: 340 to 370.0°C
Mold Temperature: 150°C
Back Pressure: 0.2 to 0.3MPa

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.