General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.37 g/cm³ Show Supplier Material materials with Density of 1.37 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.03 % Show Supplier Material materials with Water absorption of 0.03 % | ISO 62-1 | (23°C/24hrs) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 6.8 GPa Show Supplier Material materials with Elastic modulus of 6.8 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 3.1 % Show Supplier Material materials with Elongation of 3.1 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 6.1 GPa Show Supplier Material materials with Flexural modulus of 6.1 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 157 MPa Show Supplier Material materials with Flexural strength of 157 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 9 kJ/m² | ISO 180/1A | 80*10*4, -30°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 94 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 94 J/m | ASTM D 256 | notched, -30°C |
Impact strength, Izod unnotched | 23.0 °C | 38 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 38 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 616 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 616 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 24 J Show Supplier Material materials with Instrumented Impact, Total Energy of 24 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 108 MPa Show Supplier Material materials with Tensile strength of 108 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.5E-5 1/K | ASTM E 831 | 23°C to 80°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 7.4E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7.4E-5 1/K | ASTM E 831 | 23°C to 80°C | ||
Heat deflection temperature | 114 - 119 °C Show Supplier Material materials with Heat deflection temperature of 114 - 119 °C | ||||
Heat deflection temperature, 0.45 MPa | 119 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 119 °C | ASTM D 648 | 3.2 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 114 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 114 °C | ASTM D 648 | 3.2mm, unannealed | |||
Vicat softening temperature | 122 °C Show Supplier Material materials with Vicat softening temperature of 122 °C | ISO 306 | Rate B/50 | |||
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103855643- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.6mm UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant | 23.0 °C | 3.22 [-] Show Supplier Material materials with Dielectric constant of 3.22 [-] | SABIC method | 1.9 GHz |
Dielectric constant, 10GHz | 23.0 °C | 3.22 [-] Show Supplier Material materials with Dielectric constant, 10GHz of 3.22 [-] | SABIC method |
Dielectric constant, 1GHz | 23.0 °C | 3.21 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 3.21 [-] | SABIC method | 1.1 GHz |
Dielectric constant, 5GHz | 23.0 °C | 3.22 [-] Show Supplier Material materials with Dielectric constant, 5GHz of 3.22 [-] | SABIC method |
Dissipation factor | 23.0 °C | 6.5E-3 [-] Show Supplier Material materials with Dissipation factor of 6.5E-3 [-] | SABIC method |
Dissipation factor, 1GHz | 23.0 °C | 6.4E-3 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 6.4E-3 [-] | SABIC method | |
Dissipation factor, 5GHz | 23.0 °C | 6.7E-3 [-] Show Supplier Material materials with Dissipation factor, 5GHz of 6.7E-3 [-] | SABIC method |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 31 g/10min Show Supplier Material materials with Melt mass-flow rate of 31 g/10min | ASTM D 1238 | 300°C/2.16 kgf | |
Melt volume-flow rate | 13 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 13 cm³/10min | ISO 1133 | MVR at 300°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.2 % Show Supplier Material materials with Shrinkage of 0.2 % | ASTM D 955 | 24 hrs |
Shrinkage, transverse | 23.0 °C | 0.2 % Show Supplier Material materials with Shrinkage, transverse of 0.2 % | ASTM D 955 | 24 hrs |
Technological properties
Property | ||
---|---|---|
Application areas | Electronic Components | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 110°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |