NORYL GTX™ Resin GTX973 - Europe

Want to keep this datasheet? Save it now in your required format

Description

NORYL GTX™ 973 resin is a conductive, non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade is optimized to allow for in- or on-line primer-less electrostatic and powder coat painting. NORYL GTX973 resin exhibits high impact resistance and strength and is an excellent candidate for automotive painted applications such as body panels, fenders, and tank flaps.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electrical Engineering

Automotive

General Automotive Parts

Automotive Exterior

Automotive Interior

Commercial Vehicles

Other Commercial Vehicles

Construction

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.1 g/cm³ Show Supplier Material materials with Density of 1.1 g/cm³	ISO 1183
Moisture absorption	23.0 °C	1.2 % Show Supplier Material materials with Moisture absorption of 1.2 %	ISO 62 \| (23°C / 50% RH)
Relative density	23.0 °C	1.09 [-] Show Supplier Material materials with Relative density of 1.09 [-]	ASTM D 792 \|
Water absorption	23.0 °C	4.2 % Show Supplier Material materials with Water absorption of 4.2 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.3 GPa Show Supplier Material materials with Elastic modulus of 2.3 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	4 % Show Supplier Material materials with Elongation of 4 %	ISO 527 \| yield, 50 mm/min
Flexural modulus	23.0 °C	2.3 GPa Show Supplier Material materials with Flexural modulus of 2.3 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	90 MPa Show Supplier Material materials with Flexural strength of 90 MPa	ISO 178 \| yield, 2 mm/min
Impact strength, Charpy notched	23.0 °C	15 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 15 kJ/m²	ISO 179/1eA \| V-notch Edgew, 23°C, 80104 sp=62mm
Impact strength, Izod notched	23.0 °C	15 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 15 kJ/m²	ISO 180/1A \| notched 80104, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	130 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 130 J/m	ASTM D 256 \| notched, 23°C
Instrumented Impact, Total Energy	23.0 °C	50 J Show Supplier Material materials with Instrumented Impact, Total Energy of 50 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	60 MPa Show Supplier Material materials with Tensile strength of 60 MPa	ISO 527 \| yield, 50 mm/min

Thermal

Property	Temperature	Value	Comment
Ball Pressure Test		nan	IEC 60695-10-2 \| 125°C +/- 2°C
Coefficient of thermal expansion	23.0 °C	9E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 9E-5 1/K	ISO 11359-2 \| 23°C to 60°C
Coefficient of thermal expansion, transverse	23.0 °C	9E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 9E-5 1/K	ISO 11359-2 \| 23°C to 60°C
Heat deflection temperature		190 °C Show Supplier Material materials with Heat deflection temperature of 190 °C
Heat deflection temperature, 0.45 MPa		190 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 190 °C	ISO 75/Be \| Edgew 120104 sp=100mm
Vicat softening temperature		245 °C Show Supplier Material materials with Vicat softening temperature of 245 °C	ISO 306 \| Rate A/50

Electrical

Property	Temperature	Value	Comment
Volume resistivity	23.0 °C	1000 - 10000 Ω·cm Show Supplier Material materials with Volume resistivity of 1000 - 10000 Ω·cm	SABIC method

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		20 g/10min Show Supplier Material materials with Melt mass-flow rate of 20 g/10min	ASTM D 1238 \| 280°C/5.0 kgf
Melt volume-flow rate		12 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 12 cm³/10min	ISO 1133 \| MVR at 280°C/5.0 kg
Shrinkage	23.0 °C	1.4 % Show Supplier Material materials with Shrinkage of 1.4 %	SABIC method \| 3.2 mm
Shrinkage, transverse	23.0 °C	1.2 % Show Supplier Material materials with Shrinkage, transverse of 1.2 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Wheel Cover, Vertical Body Panel, Recreational Vehicle, Skid Plate, Fuel Handling, Exterior Trim, Front Grille, Furnace/Heater, Electronic Components, Enclosures, Console, Cladding, Auto Aftermarket, Building Accessory
Availability	Americas
Processing methods	Maximum Moisture Content: 0.07% Nozzle Temperature: 280 to 310.0°C Hopper Temperature: 60 to 80.0°C Middle - Zone 2 Temperature: 280 to 300.0°C Mold Temperature: 100 to 120.0°C Drying Temperature: 100 to 120.0°C Melt Temperature: 290 to 320.0°C Rear - Zone 1 Temperature: 260 to 280.0°C Drying Time: 2 to 3.0hrs Front - Zone 3 Temperature: 290 to 320.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.