General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.61 g/cm³ Show Supplier Material materials with Density of 1.61 g/cm³ | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 12.5 GPa Show Supplier Material materials with Elastic modulus of 12.5 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 3.2 % Show Supplier Material materials with Elongation of 3.2 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 11.7 GPa Show Supplier Material materials with Flexural modulus of 11.7 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 228 MPa Show Supplier Material materials with Flexural strength of 228 MPa | ISO 178 | break, 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 13 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 13 kJ/m² | ISO 179/2C | -30°C |
Impact strength, Charpy unnotched | 23.0 °C | 60 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 60 kJ/m² | ISO 179/2C | 23°C |
Impact strength, Izod notched | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 12 kJ/m² | ISO 180/1A | notched 80*10*4, -30°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 132 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 132 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched | 23.0 °C | 54 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 54 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 912 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 912 J/m | ASTM D 4812 | 23°C |
Tensile strength | 23.0 °C | 155 MPa Show Supplier Material materials with Tensile strength of 155 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.8E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.8E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 6.6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6.6E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Heat deflection temperature | 208 °C Show Supplier Material materials with Heat deflection temperature of 208 °C | ||||
Heat deflection temperature, 1.80 MPa | 208 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 208 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 75 °C Show Supplier Material materials with Relative temperature index, electrical of 75 °C | UL 746B | |||
Relative temperature index, mechanical impact | 75 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | |||
Relative temperature index, mechanical strength | 75 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 75 °C | UL 746B | |||
Vicat softening temperature | 221 °C Show Supplier Material materials with Vicat softening temperature of 221 °C | ISO 306 | Rate A/50 | |||
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103732102- - <br> UL Recognized, 94HB Flame Class Rating: 0.7mm UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant | 23.0 °C | 3.96 [-] Show Supplier Material materials with Dielectric constant of 3.96 [-] | SABIC method | 1.9 GHz |
Dielectric constant, 1GHz | 23.0 °C | 3.97 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 3.97 [-] | SABIC method | 1.1 GHz |
Dielectric constant, 5GHz | 23.0 °C | 3.96 [-] Show Supplier Material materials with Dielectric constant, 5GHz of 3.96 [-] | SABIC method |
Dissipation factor | 23.0 °C | 0.01 [-] Show Supplier Material materials with Dissipation factor of 0.01 [-] | SABIC method |
Dissipation factor, 1GHz | 23.0 °C | 0.01 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 0.01 [-] | SABIC method | |
Dissipation factor, 5GHz | 23.0 °C | 9E-3 [-] Show Supplier Material materials with Dissipation factor, 5GHz of 9E-3 [-] | SABIC method |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 43 g/10min Show Supplier Material materials with Melt mass-flow rate of 43 g/10min | ASTM D 1238 | 275°C/5 kgf | |
Melt volume-flow rate | 17 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 17 cm³/10min | ISO 1133 | MVR at 250°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.27 % Show Supplier Material materials with Shrinkage of 0.27 % | SABIC method |
Shrinkage, transverse | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage, transverse of 0.5 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Electronic Components, Wireless Communications | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 100 to 120.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |