General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.35 g/cm³ Show Supplier Material materials with Density of 1.35 g/cm³ | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.03 % Show Supplier Material materials with Moisture absorption of 0.03 % | ISO 62 | (23°C / 50% RH) |
Water absorption | 23.0 °C | 0.07 % Show Supplier Material materials with Water absorption of 0.07 % | ISO 62-1 | (23°C/saturated) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 6.8 GPa Show Supplier Material materials with Elastic modulus of 6.8 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 2.6 % Show Supplier Material materials with Elongation of 2.6 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 6.2 GPa Show Supplier Material materials with Flexural modulus of 6.2 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 165 MPa Show Supplier Material materials with Flexural strength of 165 MPa | ISO 178 | break, 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 14 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 14 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Impact strength, Charpy unnotched | 23.0 °C | 67 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 67 kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, -30°C |
Impact strength, Izod notched | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 9 kJ/m² | ISO 180/1A | notched 80*10*3, -30°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 150 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 150 J/m | ASTM D 256 |
Impact strength, Izod unnotched | 23.0 °C | 56 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 56 kJ/m² | ISO 180/1U | unnotched 80*10*4, -30°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 715 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 715 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 21 J Show Supplier Material materials with Instrumented Impact, at Peak of 21 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 112 MPa Show Supplier Material materials with Tensile strength of 112 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.6E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 7.3E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7.3E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | ||||
Glow Wire Ignition Temperature | 850 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 850 °C | IEC 60695-2-13 | 0.6 mm | |||
Heat deflection temperature | 117 - 121 °C Show Supplier Material materials with Heat deflection temperature of 117 - 121 °C | ||||
Heat deflection temperature, 0.45 MPa | 121 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 121 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 117 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 117 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Vicat softening temperature | 131 °C Show Supplier Material materials with Vicat softening temperature of 131 °C | ISO 306 | Rate A/50 | |||
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=102099701- - <br> Glow Wire Ignitability Temperature, 1.5 mm: 875°C IEC 60695-2-13 <br> Glow Wire Flammability Index, 1.5 mm: 960°C IEC 60695-2-12 <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.6mm UL 94 <br> UL Recognized, 94V-1 Flame Class Rating: ≥0.4mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.3mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.3mm UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 3 V Show Supplier Material materials with Comparative tracking index of 3 V | UL 746A | (UL) {PLC} |
Dielectric constant | 23.0 °C | 3.28 [-] Show Supplier Material materials with Dielectric constant of 3.28 [-] | SABIC method | 1.9 GHz |
Dielectric constant, 10GHz | 23.0 °C | 3.27 [-] Show Supplier Material materials with Dielectric constant, 10GHz of 3.27 [-] | SABIC method |
Dielectric constant, 1GHz | 23.0 °C | 3.24 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 3.24 [-] | SABIC method | 1.1 GHz |
Dielectric constant, 5GHz | 23.0 °C | 3.28 [-] Show Supplier Material materials with Dielectric constant, 5GHz of 3.28 [-] | SABIC method |
Dielectric strength | 23.0 °C | 40 kV/mm Show Supplier Material materials with Dielectric strength of 40 kV/mm | IEC 60243-1 | in oil, 1.0 mm, |
Dissipation factor | 23.0 °C | 6.6E-3 [-] Show Supplier Material materials with Dissipation factor of 6.6E-3 [-] | SABIC method |
Dissipation factor, 1GHz | 23.0 °C | 6.7E-3 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 6.7E-3 [-] | SABIC method | |
Dissipation factor, 5GHz | 23.0 °C | 7E-3 [-] Show Supplier Material materials with Dissipation factor, 5GHz of 7E-3 [-] | SABIC method |
High Amp Arc Ignition | 23.0 °C | 0.6 mm Show Supplier Material materials with High Amp Arc Ignition of 0.6 mm | ≥, UL 746A | PLC 0 |
High Volt Arc Track Rate | 23.0 °C | 0 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 0 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 0.6 mm Show Supplier Material materials with Hot-Wire Ignition of 0.6 mm | ≥, UL 746A | PLC 0 |
Volume resistivity | 23.0 °C | 1.00E+16 - 1.00E+17 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+16 - 1.00E+17 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 24 g/10min Show Supplier Material materials with Melt mass-flow rate of 24 g/10min | ASTM D 1238 | 300°C/2.16 kgf | |
Melt volume-flow rate | 10 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 10 cm³/10min | ISO 1133 | MVR at 300°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.2 % Show Supplier Material materials with Shrinkage of 0.2 % | ASTM D 955 | 24 hrs |
Shrinkage, transverse | 23.0 °C | 0.2 % Show Supplier Material materials with Shrinkage, transverse of 0.2 % | ASTM D 955 | 24 hrs |
Technological properties
Property | ||
---|---|---|
Application areas | Personal Computing, Wireless Communications, Watch/Jewelry, Data Transfer, Audio | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 110°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |