LEXAN™ Copolymer FXEMPX1 - Asia

Want to keep this datasheet? Save it now in your required format

Description

LEXAN FXEMPX1 polycarbonate (PC) siloxane copolymer resin is a UV stabilized injection molding (IM) grade with release properties. This resin offers good low temperature ductility in combination with high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard IM PC resins. LEXAN FXEMPX1 resin is a general purpose product available in limited colors and may be an excellent candidate for a broad range of applications.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electronics

Display Devices

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.19 g/cm³ Show Supplier Material materials with Density of 1.19 g/cm³	ISO 1183
Moisture absorption	23.0 °C	0.09 % Show Supplier Material materials with Moisture absorption of 0.09 %	ISO 62 \| (23°C / 50% RH)
Relative density	23.0 °C	1.18 [-] Show Supplier Material materials with Relative density of 1.18 [-]	ASTM D 792
Water absorption	23.0 °C	0.12 % Show Supplier Material materials with Water absorption of 0.12 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.1 GPa Show Supplier Material materials with Elastic modulus of 2.1 GPa	ASTM D 638 \| 50 mm/min
Elongation	23.0 °C	4.8 % Show Supplier Material materials with Elongation of 4.8 %	ASTM D 638 \| yld, Type I, 50 mm/min
Flexural modulus	23.0 °C	2.1 GPa Show Supplier Material materials with Flexural modulus of 2.1 GPa	ASTM D 790 \| 1.3 mm/min, 50 mm span
Flexural strength	23.0 °C	86 MPa Show Supplier Material materials with Flexural strength of 86 MPa	ASTM D 790 \| yld, 1.3 mm/min, 50 mm span
Impact strength, Izod notched	23.0 °C	750 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 750 kJ/m²	ASTM D 256 \| notched, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	750 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 750 J/m	ASTM D 256
Instrumented Impact, Total Energy	23.0 °C	70 J Show Supplier Material materials with Instrumented Impact, Total Energy of 70 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	57 MPa Show Supplier Material materials with Tensile strength of 57 MPa	ASTM D 638 \| yld, Type I, 50 mm/min

Thermal

Property	Value	Comment
Ball Pressure Test	pass	IEC 60695-10-2 \| 125°C +/- 2°C
Heat deflection temperature	116 °C Show Supplier Material materials with Heat deflection temperature of 116 °C
Heat deflection temperature, 1.80 MPa	116 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 116 °C	ASTM D 648 \| 3.2mm, unannealed
Relative temperature index, electrical	80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C	UL 746B
Relative temperature index, mechanical impact	80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C	UL 746B
Relative temperature index, mechanical strength	80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C	UL 746B
Vicat softening temperature	139 °C Show Supplier Material materials with Vicat softening temperature of 139 °C	ISO 306 \| Rate B/120
Flammability	UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=102229900- - <br> UL Recognized, 94HB Flame Class Rating: 0.5mm UL 94

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		18 g/10min Show Supplier Material materials with Melt mass-flow rate of 18 g/10min	ASTM D 1238 \| 300°C/1.2 kgf
Melt volume-flow rate		17 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 17 cm³/10min	ISO 1133 \| MVR at 300°C/1.2 kg
Shrinkage	23.0 °C	0.4 % Show Supplier Material materials with Shrinkage of 0.4 %	SABIC method \| 3.2 mm
Shrinkage, transverse	23.0 °C	0.4 % Show Supplier Material materials with Shrinkage, transverse of 0.4 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Wireless Communications, Wearables
Availability	Asia
Processing methods	Vent Depth: 0.025 to 0.076mm Rear - Zone 1 Temperature: 270 to 295.0°C Drying Time (Cumulative): 48hrs Shot to Cylinder Size: 40 to 60.0% Back Pressure: 0.3 to 0.7MPa Melt Temperature: 295 to 315.0°C Nozzle Temperature: 290 to 310.0°C Maximum Moisture Content: 0.02% Drying Time: 3 to 4.0hrs Front - Zone 3 Temperature: 295 to 315.0°C Drying Temperature: 120°C Screw Speed: 40 to 70.0rpm Middle - Zone 2 Temperature: 280 to 305.0°C Mold Temperature: 70 to 95.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.