General
Property | Temperature | Value | Comment |
---|---|---|---|
Relative density | 23.0 °C | 1.2 [-] Show Supplier Material materials with Relative density of 1.2 [-] | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.5 GPa Show Supplier Material materials with Elastic modulus of 2.5 GPa | ASTM D 638 | 50 mm/min |
Elongation | 23.0 °C | 40 % Show Supplier Material materials with Elongation of 40 % | ASTM D 638 | brk, Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 2.4 GPa Show Supplier Material materials with Flexural modulus of 2.4 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Flexural strength | 23.0 °C | 90 MPa Show Supplier Material materials with Flexural strength of 90 MPa | ASTM D 790 | yld, 1.3 mm/min, 50 mm span |
Impact strength, Izod notched | 23.0 °C | 85 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 85 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 85 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 85 J/m | ASTM D 256 |
Instrumented Impact, Total Energy | 23.0 °C | 58 J Show Supplier Material materials with Instrumented Impact, Total Energy of 58 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 42 MPa Show Supplier Material materials with Tensile strength of 42 MPa | ASTM D 638 | brk, Type I, 50 mm/min |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature | 77 °C Show Supplier Material materials with Heat deflection temperature of 77 °C | ||
Heat deflection temperature, 1.80 MPa | 77 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 77 °C | ASTM D 648 | 3.2mm, unannealed | |
Relative temperature index, electrical | 75 °C Show Supplier Material materials with Relative temperature index, electrical of 75 °C | UL 746B | |
Relative temperature index, mechanical impact | 75 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | |
Relative temperature index, mechanical strength | 75 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 75 °C | UL 746B | |
Vicat softening temperature | 101 °C Show Supplier Material materials with Vicat softening temperature of 101 °C | ASTM D 1525 | Rate B/50 | |
Flammability | UL Recognized, 94HB Flame Class Rating: ≥0.4mm UL 94 <br> UL Recognized, 94V-1 Flame Class Rating: ≥1.1mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=102563505- - |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 30 g/10min Show Supplier Material materials with Melt mass-flow rate of 30 g/10min | ASTM D 1238 | 265°C/5.0 kgf | |
Shrinkage | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage of 0.5 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Personal Computing | |
Availability | Asia | |
Processing methods | Maximum Moisture Content: 0.04% | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |