Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.19 g/cm³ Show Supplier Material materials with Density of 1.19 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.09 % Show Supplier Material materials with Moisture absorption of 0.09 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.19 [-] Show Supplier Material materials with Relative density of 1.19 [-] | ASTM D 792 | |
Water absorption | 23.0 °C | 0.24 % Show Supplier Material materials with Water absorption of 0.24 % | ISO 62-1 | (23°C/saturated) |
Mechanical
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.4 GPa Show Supplier Material materials with Elastic modulus of 2.4 GPa | ISO 527 | 1 mm/min | ||
Elongation | 23.0 °C | 118.6 % Show Supplier Material materials with Elongation of 118.6 % | ISO 527 | break, 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.3 GPa Show Supplier Material materials with Flexural modulus of 2.3 GPa | ISO 178 | 2 mm/min | ||
Flexural strength | 23.0 °C | 92 MPa Show Supplier Material materials with Flexural strength of 92 MPa | ISO 178 | yield, 2 mm/min | ||
Hardness, Rockwell L | 23.0 °C | 90 [-] Show Supplier Material materials with Hardness, Rockwell L of 90 [-] | ASTM D 785 | ||
Impact strength, Charpy notched | 23.0 °C | 60 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 60 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, 23°C | ||
Impact strength, Izod notched | 23.0 °C | 11 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 11 kJ/m² | ISO 180/1A | 80*10*4, -30°C | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 220 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 220 J/m | ASTM D 256 | ||
Instrumented Impact, Total Energy | 23.0 °C | 79 J Show Supplier Material materials with Instrumented Impact, Total Energy of 79 J | ASTM D 3763 | 23°C | ||
Tensile strength | 23.0 °C | 59 MPa Show Supplier Material materials with Tensile strength of 59 MPa | ISO 527 | yield, 50 mm/min | ||
Impact strength, Charpy unnotched | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, -30°C | ||||
Impact strength, Izod unnotched | ISO 180/1U | 80*10*3, 23°C | ||||
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Ball Pressure Test | PASS | IEC 60695-10-2 | 125°C +/- 2°C | |
Coefficient of thermal expansion | 23.0 °C | 6.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 6.5E-5 1/K | ISO 11359-2 | 23°C to 80°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 7.4E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7.4E-5 1/K | ISO 11359-2 | 23°C to 80°C |
Heat deflection temperature | 117 °C Show Supplier Material materials with Heat deflection temperature of 117 °C | ||
Heat deflection temperature, 1.80 MPa | 117 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 117 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Vicat softening temperature | 140 °C Show Supplier Material materials with Vicat softening temperature of 140 °C | ISO 306 | Rate B/120 |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 1.00E+15 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+15 Ω | >, ASTM D 257 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm | >, ASTM D 257 |
Optical
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt mass-flow rate | 35 g/10min Show Supplier Material materials with Melt mass-flow rate of 35 g/10min | ASTM D 1238 | 300°C/1.2 kgf | |
Melt volume-flow rate | 33 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 33 cm³/10min | ISO 1133 | MVR at 300°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.4 % Show Supplier Material materials with Shrinkage of 0.4 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.4 % Show Supplier Material materials with Shrinkage, transverse of 0.4 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Lab Ware and Clinical Diagnostics, Renal and Blood Handling, Monitoring and Imaging, Wireless Communications | |
| Availability | Europe | |
| Processing methods | Melt Temperature: 295 to 315.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |