General
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of friction | 0.2 [-] Show Supplier Material materials with Coefficient of friction of 0.2 [-] | ||
Coefficient of friction, kinetic | 0.2 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.2 [-] | ASTM D 3702 Modified: Manual | |
Density | 23.0 °C | 1.27 g/cm³ Show Supplier Material materials with Density of 1.27 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.4 GPa Show Supplier Material materials with Elastic modulus of 2.4 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 5.1 % Show Supplier Material materials with Elongation of 5.1 % | ISO 527 | yield, 5 mm/min |
Flexural modulus | 23.0 °C | 2.7 GPa Show Supplier Material materials with Flexural modulus of 2.7 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 82 MPa Show Supplier Material materials with Flexural strength of 82 MPa | ISO 178 | yield, 2 mm/min |
Impact strength, Izod notched | 23.0 °C | 6 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 6 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Tensile strength | 23.0 °C | 56 MPa Show Supplier Material materials with Tensile strength of 56 MPa | ISO 527 | yield, 5 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 9E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 9E-5 1/K | ISO 11359-2 | 23°C to 60°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 8.8E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 8.8E-5 1/K | ISO 11359-2 | 23°C to 60°C |
Heat deflection temperature | 128 - 139 °C Show Supplier Material materials with Heat deflection temperature of 128 - 139 °C | ||
Heat deflection temperature, 0.45 MPa | 139 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 139 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 128 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 128 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Shrinkage | 23.0 °C | 0.7 % Show Supplier Material materials with Shrinkage of 0.7 % | SABIC method | on tensile bar |
Technological properties
Property | ||
---|---|---|
Application areas | ATM/Ticket Machine, Document Handling, Personal Computing | |
Availability | Europe,Americas | |
Processing methods | Melt Temperature: 300 to 315.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |