FLEX NORYL™ Resin WCV072 - Americas

Want to keep this datasheet? Save it now in your required format

Description

FLEX NORYL™ WCV072 resin is a flexible, non-reinforced extrusion grade of Polyphenylene Ether (PPE) + Thermoplastic Elastomer (TPE) with a Shore D Hardness rating of 72. FLEX NORYL WCV072 resin was developed for evaluation in automotive wire + cable applications requiring ISO6722 Class A or B. It exhibits ultra-thin wall capability, good scratch abrasion and pinch resistance, high dimensional stability, low shrinkage and warpage, very low water absorption, chemical resistance, and good dielectric strength. Processing is typically conducted on standard extrusion equipment, and UL 1581 testing is conducted on 2.0mm wire with 0.12mm X 20 stranded copper conductor.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electrical Engineering

Automotive

General Automotive Parts

Automotive Exterior

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.03 g/cm³ Show Supplier Material materials with Density of 1.03 g/cm³	ISO 1183
Moisture absorption	23.0 °C	0.05 % Show Supplier Material materials with Moisture absorption of 0.05 %	ISO 62 \| (23°C / 50% RH)
Relative density	23.0 °C	1.03 [-] Show Supplier Material materials with Relative density of 1.03 [-]	ASTM D 792 \|
Water absorption	23.0 °C	0.12 % Show Supplier Material materials with Water absorption of 0.12 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	1.8 GPa Show Supplier Material materials with Elastic modulus of 1.8 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	46 % Show Supplier Material materials with Elongation of 46 %	ISO 527 \| break, 50 mm/min
Flexural modulus	23.0 °C	1.7 GPa Show Supplier Material materials with Flexural modulus of 1.7 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	59 MPa Show Supplier Material materials with Flexural strength of 59 MPa	ISO 178 \| yield, 2 mm/min
Impact strength, Charpy notched	23.0 °C	33 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 33 kJ/m²	ISO 179/1eA \| V-notch Edgew 80104 sp=62mm, 23°C
Impact strength, Izod notched	23.0 °C	36 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 36 kJ/m²	ISO 180/1A \| notched 80104, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	67 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 67 J/m	ASTM D 256
Instrumented Impact, Total Energy	23.0 °C	45 J Show Supplier Material materials with Instrumented Impact, Total Energy of 45 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	44 MPa Show Supplier Material materials with Tensile strength of 44 MPa	ISO 527 \| yield, 50 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	8.4E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 8.4E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Coefficient of thermal expansion, transverse	23.0 °C	1.11E-4 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 1.11E-4 1/K	ISO 11359-2 \| -40°C to 40°C
Heat deflection temperature		98 °C Show Supplier Material materials with Heat deflection temperature of 98 °C
Heat deflection temperature, 1.80 MPa		98 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 98 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Vicat softening temperature		114 °C Show Supplier Material materials with Vicat softening temperature of 114 °C	ISO 306 \| Rate B/50

Rheological Properties

Property	Value	Comment
Melt mass-flow rate	13.8 g/10min Show Supplier Material materials with Melt mass-flow rate of 13.8 g/10min	ASTM D 1238 \| 280°C/5.0 kgf
Melt volume-flow rate	13 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 13 cm³/10min	ISO 1133 \| MVR at 280°C/5.0 kg

Technological properties

Property
Application areas	Auto Electrical, Auto Aftermarket, Wire & cable
Availability	Europe,Asia,Americas
Processing methods	Water Bath Temperature: 15 to 80.0°C Neck Temperature: 250 to 285.0°C Melt Temperature: 250 to 285.0°C Drying Temperature: 60 to 80.0°C Maximum Moisture Content: 0.02% Head Zone Temperature: 250 to 285.0°C Cooling Water Air Gap: 100 to 200.0mm Drying Time: 4 to 6.0hrs Cross-head Temperature: 250 to 285.0°C Drying Time (Cumulative): 12hrs Feed Zone Temperature: 210 to 260.0°C Screw Speed: 15 to 40.0rpm Conductor Pre-heat Temperature: 80 to 150.0°C Middle Zone Temperatures: 230 to 285.0°C Screen Pack: 150 to 100.0- Die Temperature: 250 to 285.0°C Extruder Length/Diameter Ratio (L/D): 22:1 to 26:1-
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.