FLEX NORYL™ Resin WCV063 - Asia

Want to keep this datasheet? Save it now in your required format

Description

FLEX NORYL™ WCV063 resin is a flexible, non-reinforced extrusion grade of Polyphenylene Ether (PPE) + Thermoplastic Elastomer (TPE) with a Shore D Hardness rating of 63. FLEX NORYL WCV063 resin was developed for evaluation in automotive wire + cable applications requiring ISO6722 Class A or B. It exhibits ultra-thin wall capability, good scratch abrasion and pinch resistance, high dimensional stability, low shrinkage and warpage, very low water absorption, chemical resistance, and good dielectric strength. Processing is typically conducted on standard extrusion equipment, and UL 1581 testing is conducted on 2.0mm wire with 0.12mm X 20 stranded copper conductor.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electrical Engineering

Automotive

General Automotive Parts

Automotive Interior

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Relative density	23.0 °C	1.03 [-] Show Supplier Material materials with Relative density of 1.03 [-]	ASTM D 792

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	0.7 GPa Show Supplier Material materials with Elastic modulus of 0.7 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	50 % Show Supplier Material materials with Elongation of 50 %	ISO 527 \| break, 50 mm/min
Flexural modulus	23.0 °C	0.8 GPa Show Supplier Material materials with Flexural modulus of 0.8 GPa	ISO 178
Hardness, Shore D	23.0 °C	63 [-] Show Supplier Material materials with Hardness, Shore D of 63 [-]	ASTM D 2240 \| 10S reading
Impact strength, Izod notched	23.0 °C	37 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 37 kJ/m²	ISO 180/1A \| 80104, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	170 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 170 J/m	ASTM D 256 \| notched, -30°C
Tensile strength	23.0 °C	25 MPa Show Supplier Material materials with Tensile strength of 25 MPa	ISO 527 \| yield

Thermal

Property	Value	Comment
Heat deflection temperature	66 - 82 °C Show Supplier Material materials with Heat deflection temperature of 66 - 82 °C
Heat deflection temperature, 0.45 MPa	82 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 82 °C	ASTM D 648 \| 3.2 mm, unannealed
Heat deflection temperature, 1.80 MPa	66 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 66 °C	ISO 75/Af \| Flatw 80104 sp=64mm

Electrical

Property	Temperature	Value	Comment
Dielectric constant, 1GHz	23.0 °C	2.47 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 2.47 [-]	ASTM D 150
Dissipation factor, 1GHz	23.0 °C	3.2E-3 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 3.2E-3 [-]	ASTM D 150

Rheological Properties

Property	Value	Comment
Melt mass-flow rate	33 g/10min Show Supplier Material materials with Melt mass-flow rate of 33 g/10min	ASTM D 1238 \| 280°C/5.0 kgf

Technological properties

Property
Application areas	Airbag, Auto Electrical, Wire & cable
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 80 to 100.0°C Die Temperature: 280 to 300.0°C Extruder Length/Diameter Ratio (L/D): >24:1- Drying Time (Cumulative): 8hrs Neck Temperature: 280 to 300.0°C Melt Temperature: 280 to 300.0°C Drying Time: 4 to 6.0hrs Middle Zone Temperatures: 270 to 300.0°C Cooling Water Air Gap: 100 to 1000.0mm Conductor Pre-heat Temperature: 100 to 150.0°C Screw Speed: 5 to 60.0rpm Water Bath Temperature: 15 to 30.0°C Maximum Moisture Content: 0.02% Cross-head Temperature: 280 to 300.0°C Head Zone Temperature: 280 to 300.0°C Feed Zone Temperature: 200 to 260.0°C Screen Pack: 60/200/60- Compression Ratio: 2:1-3:1-
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.