LNP™ THERMOCOMP™ Compound RC003SXS

Want to keep this datasheet? Save it now in your required format

Description

LNP THERMOCOMP RC003SXS is a compound based on PA 66 resin containing Carbon fiber. Added features include: Electrically Conductive, Heat Stabilized

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.19 g/cm³ Show Supplier Material materials with Density of 1.19 g/cm³	ISO 1183
Limiting oxygen index	23.0 °C	28 % Show Supplier Material materials with Limiting oxygen index of 28 %
Water absorption	23.0 °C	5.5 % Show Supplier Material materials with Water absorption of 5.5 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	13 GPa Show Supplier Material materials with Elastic modulus of 13 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	2 % Show Supplier Material materials with Elongation of 2 %	ISO 527 \| break, 5 mm/min
Flexural modulus	23.0 °C	10 GPa Show Supplier Material materials with Flexural modulus of 10 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	230 MPa Show Supplier Material materials with Flexural strength of 230 MPa	ISO 178 \| break, 2 mm/min
Hardness, Rockwell L	23.0 °C	105 [-] Show Supplier Material materials with Hardness, Rockwell L of 105 [-]	ISO 2039-2
Impact strength, Izod notched	23.0 °C	5 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m²	ISO 180/1A \| notched 80104, 23°C
Tensile strength	23.0 °C	170 MPa Show Supplier Material materials with Tensile strength of 170 MPa	ISO 527 \| break, 5 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	2E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2E-5 1/K	ISO 11359-2 \| 23°C to 60°C
Coefficient of thermal expansion, transverse	23.0 °C	1.1E-4 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 1.1E-4 1/K	ISO 11359-2 \| 23°C to 60°C
Heat deflection temperature		250 - 252 °C Show Supplier Material materials with Heat deflection temperature of 250 - 252 °C
Heat deflection temperature, 0.45 MPa		252 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 252 °C	ISO 75/Be \| Edgew 120104 sp=100mm
Heat deflection temperature, 1.80 MPa		250 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 250 °C	ISO 75/Ae \| Edgew 120104 sp=100mm
Vicat softening temperature		255 °C Show Supplier Material materials with Vicat softening temperature of 255 °C	ISO 306 \| Rate B/120
Flammability	UL Compliant, 94HB Flame Class Rating: 1.6mm UL 94 by SABIC-IP

Electrical

Property	Temperature	Value	Comment
Sheet resistivity, ROA	23.0 °C	178000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 178000 Ω	IEC 60093
Volume resistivity	23.0 °C	178000 Ω·cm Show Supplier Material materials with Volume resistivity of 178000 Ω·cm	IEC 60093

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.1 % Show Supplier Material materials with Shrinkage of 0.1 %	SABIC method \| on tensile bar

Technological properties

Property
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 120°C Drying Time: 2 to 4.0hrs Maximum Moisture Content: 0.02% Melt Temperature: 320 to 360.0°C Nozzle Temperature: 280 to 320.0°C Front - Zone 3 Temperature: 320 to 360.0°C Middle - Zone 2 Temperature: 320 to 360.0°C Rear - Zone 1 Temperature: 280 to 320.0°C Hopper Temperature: 60 to 90.0°C Mold Temperature: 80 to 100.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.