General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.56 g/cm³ Show Supplier Material materials with Density of 1.56 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 4.5 % Show Supplier Material materials with Water absorption of 4.5 % | ISO 62-1 | (23°C/saturated) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 6.2 GPa Show Supplier Material materials with Elastic modulus of 6.2 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 2.5 % Show Supplier Material materials with Elongation of 2.5 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 6 GPa Show Supplier Material materials with Flexural modulus of 6 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 140 MPa Show Supplier Material materials with Flexural strength of 140 MPa | ISO 178 | break, 2 mm/min |
Impact strength, Izod notched | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Tensile strength | 23.0 °C | 85 MPa Show Supplier Material materials with Tensile strength of 85 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 3E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 3E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 3E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Heat deflection temperature | 175 - 245 °C Show Supplier Material materials with Heat deflection temperature of 175 - 245 °C | ||||
Heat deflection temperature, 0.45 MPa | 245 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 245 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |||
Heat deflection temperature, 1.80 MPa | 175 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 175 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |||
Vicat softening temperature | 255 °C Show Supplier Material materials with Vicat softening temperature of 255 °C | ISO 306 | Rate A/50 | |||
Flammability | UL Compliant, 94HB Flame Class Rating: 1.6mm UL 94 by SABIC-IP |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 400 V Show Supplier Material materials with Comparative tracking index of 400 V | IEC 60112 | M |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Shrinkage | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage of 0.5 % | SABIC method | on tensile bar |
Technological properties
Property | ||
---|---|---|
Application areas | Electronic Components | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 75 to 85.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |