LNP™ LUBRICOMP™ Compound OCL36A - Europe

Want to keep this datasheet? Save it now in your required format

Description

LNP LUBRICOMP* OCL36A is a compound based on PPS - Branched resin containing 30% Carbon Fiber, 15% PTFE. Added features of this material include: Electrically Conductive, Wear Resistant.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electronics

Display Devices

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	0.7 % Show Supplier Material materials with Elongation of 0.7 %	ISO 527 \| break, 5 mm/min
Flexural modulus	23.0 °C	21.2 GPa Show Supplier Material materials with Flexural modulus of 21.2 GPa	ISO 178 \| 2 mm/min
Impact strength, Izod notched	23.0 °C	6 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 6 kJ/m²	ISO 180/1A \| notched 80103, -40°C
Tensile strength	23.0 °C	153 MPa Show Supplier Material materials with Tensile strength of 153 MPa	ISO 527 \| break, 5 mm/min

Thermal

Property	Value	Comment
Heat deflection temperature	255 °C Show Supplier Material materials with Heat deflection temperature of 255 °C
Heat deflection temperature, 1.80 MPa	255 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 255 °C	ISO 75/Af \| Flatw 80104 sp=64mm

Technological properties

Property
Application areas	Document Handling, Data Management, Oil/Gas
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 120 to 150.0°C Middle - Zone 2 Temperature: 320 to 330.0°C Rear - Zone 1 Temperature: 305 to 315.0°C Front - Zone 3 Temperature: 330 to 345.0°C Screw Speed: 30 to 60.0rpm Melt Temperature: 315 to 320.0°C Drying Time: 4hrs Back Pressure: 0.2 to 0.3MPa Mold Temperature: 140 to 165.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.