LEXAN™ Copolymer EXL9330S - Americas

Want to keep this datasheet? Save it now in your required format

Description

Opaque PC-Siloxane copolymer with excellent processability. UV stabilized. UL rated V-0/5VA/CTI-PLC-2. Available in limited colors; please contact your SABIC IP representative

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electrical Engineering

Construction

Lighting

Railway

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.24 g/cm³ Show Supplier Material materials with Density of 1.24 g/cm³	ISO 1183
Moisture absorption	23.0 °C	0.05 % Show Supplier Material materials with Moisture absorption of 0.05 %	ISO 62 \| (23°C / 50% RH)
Relative density	23.0 °C	1.24 [-] Show Supplier Material materials with Relative density of 1.24 [-]	ASTM D 792 \|
Water absorption	23.0 °C	0.12 % Show Supplier Material materials with Water absorption of 0.12 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.2 GPa Show Supplier Material materials with Elastic modulus of 2.2 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	6 % Show Supplier Material materials with Elongation of 6 %	ISO 527 \| yield, 50 mm/min
Flexural modulus	23.0 °C	2.2 GPa Show Supplier Material materials with Flexural modulus of 2.2 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	86 MPa Show Supplier Material materials with Flexural strength of 86 MPa	ISO 178 \| yield, 2 mm/min
Impact strength, Charpy notched	23.0 °C	70 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 70 kJ/m²	ISO 179/1eA \| V-notch Edgew 80103 sp=62mm, 23°C
Impact strength, Izod notched	23.0 °C	75 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 75 kJ/m²	ISO 180/1A \| 80103, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	700 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 700 J/m	ASTM D 256
Tensile strength	23.0 °C	59 MPa Show Supplier Material materials with Tensile strength of 59 MPa	ISO 527 \| yield, 50 mm/min
Impact strength, Charpy unnotched	ISO 179/1eU \| Unnotch Edgew 80103 sp=62mm, -30°C
Impact strength, Izod unnotched	ISO 180/1U \| unnotched 80103, -30°C

Thermal

Property	Value	Comment
Ball Pressure Test	nan	IEC 60695-10-2 \| 125°C +/- 2°C
Heat deflection temperature	126 - 139 °C Show Supplier Material materials with Heat deflection temperature of 126 - 139 °C
Heat deflection temperature, 0.45 MPa	139 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 139 °C	ISO 75/Be \| Edgew 120104 sp=100mm
Heat deflection temperature, 1.80 MPa	126 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 126 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Vicat softening temperature	147 °C Show Supplier Material materials with Vicat softening temperature of 147 °C	ISO 306 \| Rate B/120

Electrical

Property	Temperature	Value	Comment
Comparative tracking index	23.0 °C	2 V Show Supplier Material materials with Comparative tracking index of 2 V	UL 746A \| (UL) {PLC}

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		8 g/10min Show Supplier Material materials with Melt mass-flow rate of 8 g/10min	ASTM D 1238 \| 300°C/1.2 kgf
Melt volume-flow rate		7 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 7 cm³/10min	ISO 1133 \| MVR at 300°C/1.2 kg
Shrinkage	23.0 °C	0.4 % Show Supplier Material materials with Shrinkage of 0.4 %	SABIC method \| 3.2 mm
Shrinkage, transverse	23.0 °C	0.4 % Show Supplier Material materials with Shrinkage, transverse of 0.4 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Photovoltaic Components, Rail Cabin Interiors, Non-LED Lighting, Electronic Components, Air Conditioning
Availability	Europe,Asia,Americas
Processing methods	Middle - Zone 2 Temperature: 280 to 305.0°C Rear - Zone 1 Temperature: 275 to 295.0°C Drying Temperature: 120°C Nozzle Temperature: 290 to 310.0°C Shot to Cylinder Size: 40 to 60.0% Screw Speed: 40 to 70.0rpm Drying Time (Cumulative): 48hrs Melt Temperature: 295 to 315.0°C Front - Zone 3 Temperature: 295 to 315.0°C Drying Time: 3 to 4.0hrs Back Pressure: 0.3 to 0.7MPa Mold Temperature: 70 to 95.0°C Vent Depth: 0.025 to 0.076mm Maximum Moisture Content: 0.02%
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.