General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.2 g/cm³ Show Supplier Material materials with Density of 1.2 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.35 % Show Supplier Material materials with Moisture absorption of 0.35 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.2 [-] Show Supplier Material materials with Relative density of 1.2 [-] | ASTM D 792 | |
Specific volume | 23.0 °C | 0.83 cm³/g Show Supplier Material materials with Specific volume of 0.83 cm³/g | ASTM D 792 |
Water absorption | 23.0 °C | 0.16 % Show Supplier Material materials with Water absorption of 0.16 % | ISO 62-1 | (23°C/saturated) |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.2 GPa Show Supplier Material materials with Elastic modulus of 2.2 GPa | ISO 527 | 1 mm/min | ||
Elongation | 23.0 °C | 85 % Show Supplier Material materials with Elongation of 85 % | ISO 527 | break, 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.1 GPa Show Supplier Material materials with Flexural modulus of 2.1 GPa | ISO 178 | 2 mm/min | ||
Flexural strength | 23.0 °C | 66 MPa Show Supplier Material materials with Flexural strength of 66 MPa | ISO 178 | yield, 2 mm/min | ||
Hardness, Rockwell M | 23.0 °C | 85 [-] Show Supplier Material materials with Hardness, Rockwell M of 85 [-] | ASTM D 785 | | ||
Hardness, Rockwell R | 23.0 °C | 122 [-] Show Supplier Material materials with Hardness, Rockwell R of 122 [-] | ASTM D 785 | ||
Impact strength, Charpy notched | 23.0 °C | 13 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 13 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, -30°C | ||
Impact strength, Izod notched | 23.0 °C | 53 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 53 kJ/m² | ISO 180/1A | 80*10*3, 23°C | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 600 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 600 J/m | ASTM D 256 | ||
Instrumented Impact, Total Energy | 23.0 °C | 120 J Show Supplier Material materials with Instrumented Impact, Total Energy of 120 J | ASTM D 3763 | 23°C | ||
Tensile strength | 23.0 °C | 60 MPa Show Supplier Material materials with Tensile strength of 60 MPa | ISO 527 | break, 50 mm/min | ||
Impact strength, Charpy unnotched | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, -30°C | ||||
Impact strength, Izod unnotched | ISO 180/1U | 80*10*3, 23°C | ||||
Impact strength, Izod unnotched, ASTM | ASTM D 4812 | 23°C |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 6E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Heat deflection temperature | 125 °C Show Supplier Material materials with Heat deflection temperature of 125 °C | ||
Heat deflection temperature, 1.80 MPa | 125 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 125 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Specific heat capacity | 23.0 °C | 1.25E-3 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 1.25E-3 J/(kg·K) | ASTM C 351 |
Thermal conductivity | 23.0 °C | 0.21 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.21 W/(m·K) | ASTM C177 |
Vicat softening temperature | 154 °C Show Supplier Material materials with Vicat softening temperature of 154 °C | ISO 306 | Rate B/50 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 1MHz | 23.0 °C | 3 [-] Show Supplier Material materials with Dielectric constant, 1MHz of 3 [-] | ASTM D 150 |
Dielectric constant, 60Hz | 23.0 °C | 3.15 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 3.15 [-] | ASTM D 150 | 50/60 Hz |
Dielectric strength | 23.0 °C | 20.2 kV/mm Show Supplier Material materials with Dielectric strength of 20.2 kV/mm | ASTM D 149 | in air, 3.2 mm |
Dissipation factor, 100Hz | 23.0 °C | 0.02 [-] Show Supplier Material materials with Dissipation factor, 100Hz of 0.02 [-] | ASTM D 150 |
Dissipation factor, 50Hz | 23.0 °C | 1.2E-3 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 1.2E-3 [-] | ASTM D 150 | 50/60 Hz |
Volume resistivity | 23.0 °C | 2.60E+17 Ω·cm Show Supplier Material materials with Volume resistivity of 2.60E+17 Ω·cm | >, ASTM D 257 |
Optical
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 6 g/10min Show Supplier Material materials with Melt mass-flow rate of 6 g/10min | ASTM D 1238 | 300°C/1.2 kgf | |
Melt volume-flow rate | 29 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 29 cm³/10min | ISO 1133 | MVR at 330°C/2.16kg | |
Shrinkage | 23.0 °C | 0.6 % Show Supplier Material materials with Shrinkage of 0.6 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Surgical Devices, Renal and Blood Handling, Pharmaceutical Manufacturing, Pharmaceutical Packaging & Drug Delivery, Medical Device | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |