General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.31 g/cm³ Show Supplier Material materials with Density of 1.31 g/cm³ | ISO 1183 |
Relative density | 23.0 °C | 1.31 [-] Show Supplier Material materials with Relative density of 1.31 [-] | ASTM D 792 | |
Water absorption | 23.0 °C | 2.3 % Show Supplier Material materials with Water absorption of 2.3 % | ISO 62-1 | (23°C/saturated) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 3.1 GPa Show Supplier Material materials with Elastic modulus of 3.1 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 7 % Show Supplier Material materials with Elongation of 7 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 2.9 GPa Show Supplier Material materials with Flexural modulus of 2.9 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 120 MPa Show Supplier Material materials with Flexural strength of 120 MPa | ISO 178 | yield, 2 mm/min |
Impact strength, Izod notched | 23.0 °C | 4 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 4 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 43 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 43 J/m | ASTM D 256 |
Tensile strength | 23.0 °C | 101 MPa Show Supplier Material materials with Tensile strength of 101 MPa | ISO 527 | yield, 5 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 5E-5 1/K | ISO 11359-2 | 23°C to 150°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 5.1E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5.1E-5 1/K | ISO 11359-2 | 23°C to 150°C |
Heat deflection temperature | 223 - 250 °C Show Supplier Material materials with Heat deflection temperature of 223 - 250 °C | ||
Heat deflection temperature, 0.45 MPa | 250 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 250 °C | ASTM D 648 | 3.2 mm, unannealed | |
Heat deflection temperature, 1.80 MPa | 223 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 223 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Vicat softening temperature | 247 °C Show Supplier Material materials with Vicat softening temperature of 247 °C | ISO 306 | Rate B/120 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 125 V Show Supplier Material materials with Comparative tracking index of 125 V | IEC 60112 | |
Dielectric constant, 1KHz | 23.0 °C | 3.5 [-] Show Supplier Material materials with Dielectric constant, 1KHz of 3.5 [-] | ASTM D 150 |
Dielectric constant, 1MHz | 23.0 °C | 3.4 [-] Show Supplier Material materials with Dielectric constant, 1MHz of 3.4 [-] | ASTM D 150 |
Dielectric strength | 23.0 °C | 25 kV/mm Show Supplier Material materials with Dielectric strength of 25 kV/mm | ASTM D 149 | in air, 1.6 mm |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 10 g/10min Show Supplier Material materials with Melt mass-flow rate of 10 g/10min | ASTM D 1238 | 367°C/6.6 kgf | |
Shrinkage | 23.0 °C | 1 % Show Supplier Material materials with Shrinkage of 1 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Non-LED Lighting, Wireless Communications, Wearables, Circuit Protection, Data Transfer, Data Management, Electronic Components, Fluid Delivery | |
Availability | Europe,Asia,Americas | |
Processing methods | Mold Temperature: 160 to 200.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |