LEXAN™ Copolymer EXL9414TRC - Asia

Want to keep this datasheet? Save it now in your required format

Description

LEXAN EXL9414TRC resin grade is a 21% PCR(Post Consumer Recycle) contain halogen-free flame retardant polycarbonate featuring transparency, -40 degree C ductility and UL-94 V0 rating for injection molding applications. Excellent impact combined with good flow, all transparent colorability for aesthetics and thin wall flame retardant makes this product an excellent candidate for thin wall applications.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electronics

Display Devices

Consumer Goods

Domestic Electrical Appliances

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.19 g/cm³ Show Supplier Material materials with Density of 1.19 g/cm³	ASTM D 792
Relative density	23.0 °C	1.19 [-] Show Supplier Material materials with Relative density of 1.19 [-]	ASTM D 792
Water absorption	23.0 °C	0.09 % Show Supplier Material materials with Water absorption of 0.09 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.2 GPa Show Supplier Material materials with Elastic modulus of 2.2 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	5.4 % Show Supplier Material materials with Elongation of 5.4 %	ISO 527 \| yield, 50 mm/min
Flexural modulus	23.0 °C	2.2 GPa Show Supplier Material materials with Flexural modulus of 2.2 GPa	ASTM D 790 \| 1.3 mm/min, 50 mm span
Flexural strength	23.0 °C	86 MPa Show Supplier Material materials with Flexural strength of 86 MPa	ASTM D 790 \| yld, 1.3 mm/min, 50 mm span
Impact strength, Charpy notched	23.0 °C	24 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 24 kJ/m²	ISO 179/1eA \| V-notch Edgew 80103 sp=62mm, -30°C
Impact strength, Izod notched	23.0 °C	58 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 58 kJ/m²	ISO 180/1A \| 80103, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	311 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 311 J/m	ASTM D 256
Instrumented Impact, Total Energy	23.0 °C	65 J Show Supplier Material materials with Instrumented Impact, Total Energy of 65 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	54 MPa Show Supplier Material materials with Tensile strength of 54 MPa	ISO 527 \| break, 50 mm/min
Impact strength, Charpy unnotched	ISO 179/1eU \| Unnotch Edgew 80103 sp=62mm, -30°C
Impact strength, Izod unnotched	ISO 180/1U \| 80103, -30°C

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	6.7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 6.7E-5 1/K	ASTM E 831 \| -40°C to 95°C
Coefficient of thermal expansion, transverse	23.0 °C	8E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 8E-5 1/K	ASTM E 831 \| -40°C to 95°C
Heat deflection temperature		110 °C Show Supplier Material materials with Heat deflection temperature of 110 °C
Heat deflection temperature, 1.80 MPa		110 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 110 °C	ASTM D 648 \| 3.2mm, unannealed
Relative temperature index, electrical		120 °C Show Supplier Material materials with Relative temperature index, electrical of 120 °C	UL 746B
Relative temperature index, mechanical impact		110 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 110 °C	UL 746B
Relative temperature index, mechanical strength		120 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 120 °C	UL 746B
Vicat softening temperature		129 °C Show Supplier Material materials with Vicat softening temperature of 129 °C	ISO 306 \| Rate B/50
Flammability	UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103258548- - <br> UL Recognized, 94V-2 Flame Class Rating: ≥1mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥1mm UL 94

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		12 g/10min Show Supplier Material materials with Melt mass-flow rate of 12 g/10min	ASTM D 1238 \| 300°C/1.2 kgf
Melt volume-flow rate		11 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 11 cm³/10min	ISO 1133 \| MVR at 300°C/1.2 kg
Shrinkage	23.0 °C	0.4 % Show Supplier Material materials with Shrinkage of 0.4 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Data Transfer, Personal Computing
Availability	Asia
Processing methods	Drying Temperature: 120°C Drying Time: 3 to 4.0hrs Maximum Moisture Content: 0.02% Melt Temperature: 295 to 315.0°C Nozzle Temperature: 290 to 310.0°C Front - Zone 3 Temperature: 295 to 315.0°C Middle - Zone 2 Temperature: 280 to 305.0°C Rear - Zone 1 Temperature: 270 to 295.0°C Mold Temperature: 70 to 110.0°C Back Pressure: 0.3 to 0.7MPa Screw Speed: 40 to 70.0rpm Shot to Cylinder Size: 40 to 60.0% Vent Depth: 0.025 to 0.076mm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.