General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.27 g/cm³ Show Supplier Material materials with Density of 1.27 g/cm³ | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 19.4 GPa Show Supplier Material materials with Elastic modulus of 19.4 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 1 % Show Supplier Material materials with Elongation of 1 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 16.5 GPa Show Supplier Material materials with Flexural modulus of 16.5 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 206 MPa Show Supplier Material materials with Flexural strength of 206 MPa | ISO 178 |
Impact strength, Izod notched | 23.0 °C | 129 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 129 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 117 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 117 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 694 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 694 J/m | ASTM D 4812 | 23°C |
Tensile strength | 23.0 °C | 130 MPa Show Supplier Material materials with Tensile strength of 130 MPa | ISO 527 | break, 5 mm/min |
Thermal
Technological properties
Property | ||
---|---|---|
Application areas | Auto Aftermarket | |
Availability | Asia,Americas | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |