Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Water absorption | 23.0 °C | 0.07 % Show Supplier Material materials with Water absorption of 0.07 % | ASTM D 570 | (23°C/24hrs) |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongation | 23.0 °C | 3 % Show Supplier Material materials with Elongation of 3 % | ISO 527 | yield, 50 mm/min |
Flexural modulus | 23.0 °C | 2.3 GPa Show Supplier Material materials with Flexural modulus of 2.3 GPa | ASTM D 790 |
Flexural strength | 23.0 °C | 68 MPa Show Supplier Material materials with Flexural strength of 68 MPa | ASTM D 790 |
Impact strength, Izod notched | 23.0 °C | 283 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 283 kJ/m² | ASTM D 256 | notched, 23°C |
Tensile strength | 23.0 °C | 50 MPa Show Supplier Material materials with Tensile strength of 50 MPa | ISO 527 | yield, 50 mm/min |
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Heat deflection temperature | 90 °C Show Supplier Material materials with Heat deflection temperature of 90 °C | ||||
Heat deflection temperature, 1.80 MPa | 90 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 90 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Relative temperature index, electrical | 95 °C Show Supplier Material materials with Relative temperature index, electrical of 95 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 95 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 95 °C | UL 746B | |||
Flammability | UL Recognized, 94-5VA Flame Class Rating: ≥2.8mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.75mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.75mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=228562- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=237048- - | ||||
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Comparative tracking index | 23.0 °C | 2 V Show Supplier Material materials with Comparative tracking index of 2 V | UL 746A | (UL) {PLC} |
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | ≥, UL 746A | PLC 2 |
High Volt Arc Track Rate | 23.0 °C | 4 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | ≥, UL 746A | PLC 2 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Shrinkage | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage of 0.5 % | SABIC method | on tensile bar |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Wireless Communications, Surgical Tray, Tray, Monitoring and Imaging, Power Manangement, Refrigerator, Document Handling, Air Conditioning, Auto Electrical, Circuit Protection, Energy Management, Enclosures, Electronic Components, Wire & cable | |
| Availability | Europe | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |