FLEX NORYL™ Resin WCP841 - Asia

Want to keep this datasheet? Save it now in your required format

Description

FLEX NORYL™ WCP841 resin is flexible, non-reinforced injection moldable blend of polyphenylene ether (PPE) + thermoplastic elastomer (TPE). This material contains non-halogenated flame retardant and carries a UL94 flame rating of V0 at 6mm. FLEX NORYL WCP841 resin is intended for evaluation in over-molding applications such as plugs, strain reliefs, and connectors. It has a Shore A Hardness reading of 84 and exhibits low specific gravity, very low water absorption, and dimensional stability.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electrical Engineering

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Relative density	23.0 °C	1.01 [-] Show Supplier Material materials with Relative density of 1.01 [-]	ASTM D 792

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	175 % Show Supplier Material materials with Elongation of 175 %	ISO 527 \| break, 50 mm/min
Flexural modulus	23.0 °C	0.1 GPa Show Supplier Material materials with Flexural modulus of 0.1 GPa	ISO 178 \| 12.5 mm/min
Hardness, Shore A	23.0 °C	84 [-] Show Supplier Material materials with Hardness, Shore A of 84 [-]	ASTM D 2240 \| 30S reading
Tensile strength	23.0 °C	7 MPa Show Supplier Material materials with Tensile strength of 7 MPa	ISO 527 \| break, 50 mm/min

Thermal

Property	Value	Comment
Brittleness temperature	-40 °C Show Supplier Material materials with Brittleness temperature of -40 °C	<, ASTM D 746
Glow Wire Ignition Temperature	750 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 750 °C	IEC 60695-2-13 \| 3.0 mm
Flammability	Glow Wire Flammability Index 750°C, passes at: 3mm IEC 60695-2-12 <br> UL Recognized, 94V-0 Flame Class Rating: ≥6mm UL 94 <br> UL Recognized, 94HB Flame Class Rating: ≥0.6mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101939210- -

Electrical

Property	Temperature	Value	Comment
Comparative tracking index	23.0 °C	0 V Show Supplier Material materials with Comparative tracking index of 0 V	UL 746A \| (UL) {PLC}
Volume resistivity	23.0 °C	7.10E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 7.10E+15 Ω·cm	ASTM D 257

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		24 g/10min Show Supplier Material materials with Melt mass-flow rate of 24 g/10min	ASTM D 1238 \| 210°C/5 kgf
Shrinkage	23.0 °C	0.95 % Show Supplier Material materials with Shrinkage of 0.95 %	ASTM D 955 \| 24 hrs
Shrinkage, transverse	23.0 °C	0.75 % Show Supplier Material materials with Shrinkage, transverse of 0.75 %	ASTM D 955 \| 24 hrs

Technological properties

Property
Application areas	Wire & cable
Availability	Asia,Americas
Processing methods	Screw Speed: 30 to 80.0rpm Front - Zone 3 Temperature: 220 to 250.0°C Back Pressure: 3 to 10.0MPa Melt Temperature: 220 to 250.0°C Rear - Zone 1 Temperature: 180 to 220.0°C Shot to Cylinder Size: 30 to 70.0% Vent Depth: 0.03 to 0.05mm Nozzle Temperature: 220 to 250.0°C Middle - Zone 2 Temperature: 210 to 240.0°C Drying Temperature: 60 to 80.0°C Drying Time: 4 to 6.0hrs Drying Time (Cumulative): 8hrs Mold Temperature: 40 to 60.0°C Maximum Moisture Content: 0.01%
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.