NORYL™ Resin N1900 - Asia

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ N1900 resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of 5VA at 3mm and V0 at 1.5mm along with UL746C Outdoor Suitability rating of F1. NORYL N1900 resin exhibits high impact strength, dimensional stability, hydrolytic stability, and very low moisture absorption. This material is an excellent candidate for a variety of applications such as solar frames, unattended power supply (UPS) inverter/charger, indoor and outdoor electrical enclosures / housings / connectors, and wall plates / sockets / switches. *this grade is also referred to as NORYL N190 in several regions.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Healthcare

Medical Equipment

Surgical Instruments

Medical Equipment General

Mechanical Systems

Industrial Machinery

Electrical Engineering

Electronics

Display Devices

Automotive

General Automotive Parts

Construction

Consumer Goods

Domestic Electrical Appliances

Show all

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Water absorption	23.0 °C	0.07 % Show Supplier Material materials with Water absorption of 0.07 %	ASTM D 570 \| (23°C/24hrs)

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	3 % Show Supplier Material materials with Elongation of 3 %	ISO 527 \| yield, 50 mm/min
Flexural modulus	23.0 °C	2.3 GPa Show Supplier Material materials with Flexural modulus of 2.3 GPa	ASTM D 790
Flexural strength	23.0 °C	68 MPa Show Supplier Material materials with Flexural strength of 68 MPa	ASTM D 790
Impact strength, Izod notched	23.0 °C	283 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 283 kJ/m²	ASTM D 256 \| notched, 23°C
Tensile strength	23.0 °C	50 MPa Show Supplier Material materials with Tensile strength of 50 MPa	ISO 527 \| yield, 50 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7E-5 1/K	ISO 11359-2 \| 23°C to 80°C
Heat deflection temperature		90 °C Show Supplier Material materials with Heat deflection temperature of 90 °C
Heat deflection temperature, 1.80 MPa		90 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 90 °C	ASTM D 648 \| 6.4 mm, unannealed

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.5 % Show Supplier Material materials with Shrinkage of 0.5 %	SABIC method \| on tensile bar

Technological properties

Property
Application areas	Wire & cable
Availability	Europe,Asia
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.