Property | Temperature | Value | Comment |
---|---|---|---|
Relative density | 23.0 °C | 1.11 [-] Show Supplier Material materials with Relative density of 1.11 [-] | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.8 GPa Show Supplier Material materials with Elastic modulus of 2.8 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 4 % Show Supplier Material materials with Elongation of 4 % | ISO 527 | break, 50 mm/min |
Flexural modulus | 23.0 °C | 2.5 GPa Show Supplier Material materials with Flexural modulus of 2.5 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 103 MPa Show Supplier Material materials with Flexural strength of 103 MPa | ISO 178 | yield, 2 mm/min |
Impact strength, Izod notched | 23.0 °C | 74 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 74 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 74 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 74 J/m | ASTM D 256 |
Instrumented Impact, Total Energy | 23.0 °C | 4 J Show Supplier Material materials with Instrumented Impact, Total Energy of 4 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 60 MPa Show Supplier Material materials with Tensile strength of 60 MPa | ISO 527 | break, 50 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 8.1E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 8.1E-5 1/K | ISO 11359-2 | 23°C to 80°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 8.6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 8.6E-5 1/K | ISO 11359-2 | 23°C to 80°C |
Heat deflection temperature | 185 °C Show Supplier Material materials with Heat deflection temperature of 185 °C | ||
Heat deflection temperature, 0.45 MPa | 185 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 185 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Vicat softening temperature | 197 °C Show Supplier Material materials with Vicat softening temperature of 197 °C | ISO 306 | Rate B/50 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Volume resistivity | 23.0 °C | 1000 - 10000 Ω·cm Show Supplier Material materials with Volume resistivity of 1000 - 10000 Ω·cm | SABIC method |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 25 g/10min Show Supplier Material materials with Melt mass-flow rate of 25 g/10min | ASTM D 1238 | 300°C/5.0 kgf | |
Shrinkage | 23.0 °C | 1 % Show Supplier Material materials with Shrinkage of 1 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Seating/Chair | |
Availability | Europe,Asia,MEA,Americas | |
Processing methods | Shot to Cylinder Size: 30 to 50.0% | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |