LNP™ STAT-KON™ Compound RX08408

Want to keep this datasheet? Save it now in your required format

Description

LNP STAT-KON RX08404 is a compound based on Nylon 66 containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Moisture absorption	23.0 °C	0.87 % Show Supplier Material materials with Moisture absorption of 0.87 %	ISO 62 \| (23°C / 50% RH)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	1.9 GPa Show Supplier Material materials with Elastic modulus of 1.9 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	26 % Show Supplier Material materials with Elongation of 26 %	ISO 527 \| break, 5 mm/min
Flexural modulus	23.0 °C	1.9 GPa Show Supplier Material materials with Flexural modulus of 1.9 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	61 MPa Show Supplier Material materials with Flexural strength of 61 MPa	ISO 178
Impact strength, Izod notched	23.0 °C	12 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 12 kJ/m²	ISO 180/1A \| notched 80104, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	141 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 141 J/m	ASTM D 256 \| notched, 23°C
Impact strength, Izod unnotched	23.0 °C	196 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 196 kJ/m²	ISO 180/1U \| 80104, 23°C
Impact strength, Izod unnotched, ASTM	23.0 °C	1720 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 1720 J/m	ASTM D 4812 \| 23°C
Instrumented Impact, Total Energy	23.0 °C	22 J Show Supplier Material materials with Instrumented Impact, Total Energy of 22 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	47 MPa Show Supplier Material materials with Tensile strength of 47 MPa	ISO 527 \| break, 5 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	1.1E-4 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.1E-4 1/K	ASTM D 696 \| -30°C to 30°C
Coefficient of thermal expansion, transverse	23.0 °C	1.14E-4 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 1.14E-4 1/K	ASTM D 696 \| -30°C to 30°C
Heat deflection temperature		117 - 165 °C Show Supplier Material materials with Heat deflection temperature of 117 - 165 °C
Heat deflection temperature, 0.45 MPa		165 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 165 °C	ISO 75/Bf \| Flatw 80104 sp=64mm
Heat deflection temperature, 1.80 MPa		117 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 117 °C	ISO 75/Af \| Flatw 80104 sp=64mm

Electrical

Property	Temperature	Value	Comment
Sheet resistivity, ROA	23.0 °C	1000 - 1000000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1000 - 1000000 Ω	ASTM D 257
Volume resistivity	23.0 °C	1000 - 1000000 Ω·cm Show Supplier Material materials with Volume resistivity of 1000 - 1000000 Ω·cm	ASTM D 257

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	3 % Show Supplier Material materials with Shrinkage of 3 %	ASTM D 955 \| 24 hrs
Shrinkage, transverse	23.0 °C	3 % Show Supplier Material materials with Shrinkage, transverse of 3 %	ASTM D 955 \| 24 hrs

Technological properties

Property
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 80°C Drying Time: 4hrs Maximum Moisture Content: 0.15 to 0.25% Melt Temperature: 280 to 305.0°C Front - Zone 3 Temperature: 295 to 305.0°C Middle - Zone 2 Temperature: 280 to 295.0°C Rear - Zone 1 Temperature: 265 to 275.0°C Mold Temperature: 95 to 110.0°C Back Pressure: 0.2 to 0.3MPa Screw Speed: 30 to 60.0rpm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.