LNP™ STAT-KON™ Compound FX98500C

Want to keep this datasheet? Save it now in your required format

Description

LNP STAT-KON FX98500C is a compound based on Polyethylene resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Automotive

General Automotive Parts

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	0.97 g/cm³ Show Supplier Material materials with Density of 0.97 g/cm³	ISO 1183
Moisture absorption	23.0 °C	0.02 % Show Supplier Material materials with Moisture absorption of 0.02 %	ISO 62 \| (23°C / 50% RH)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	0.9 GPa Show Supplier Material materials with Elastic modulus of 0.9 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	82.8 % Show Supplier Material materials with Elongation of 82.8 %	ISO 527 \| break
Flexural modulus	23.0 °C	0.9 GPa Show Supplier Material materials with Flexural modulus of 0.9 GPa	ISO 178
Flexural strength	23.0 °C	27 MPa Show Supplier Material materials with Flexural strength of 27 MPa	ISO 178
Impact strength, Izod notched	23.0 °C	5 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m²	ISO 180/1A \| 80104, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	48 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 48 J/m	ASTM D 256 \| notched, 23°C
Instrumented Impact, at Peak	23.0 °C	21 J Show Supplier Material materials with Instrumented Impact, at Peak of 21 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	14 MPa Show Supplier Material materials with Tensile strength of 14 MPa	ISO 527 \| break
Impact strength, Izod unnotched	ISO 180/1U \| 80104, 23°C
Impact strength, Izod unnotched, ASTM	ASTM D 4812 \| 23°C

Thermal

Property	Value	Comment
Heat deflection temperature	48 °C Show Supplier Material materials with Heat deflection temperature of 48 °C
Heat deflection temperature, 1.80 MPa	48 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 48 °C	ISO 75/Af \| Flatw 80104 sp=64mm

Electrical

Property	Temperature	Value	Comment
Sheet resistivity, ROA	23.0 °C	100 - 100000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 100 - 100000 Ω	ASTM D 257
Volume resistivity	23.0 °C	100 - 100000 Ω·cm Show Supplier Material materials with Volume resistivity of 100 - 100000 Ω·cm	ASTM D 257

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	2 % Show Supplier Material materials with Shrinkage of 2 %	ISO 294 \| 24 hrs
Shrinkage, transverse	23.0 °C	2 % Show Supplier Material materials with Shrinkage, transverse of 2 %	ISO 294 \| 24 hrs

Technological properties

Property
Application areas	Fuel Handling
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 80°C Drying Time: 4hrs Melt Temperature: 230°C Front - Zone 3 Temperature: 220 to 230.0°C Middle - Zone 2 Temperature: 210 to 220.0°C Rear - Zone 1 Temperature: 195 to 205.0°C Mold Temperature: 40 to 55.0°C Back Pressure: 0.2 to 0.3MPa Screw Speed: 30 to 60.0rpm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.