Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.14 g/cm³ Show Supplier Material materials with Density of 1.14 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.06 % Show Supplier Material materials with Moisture absorption of 0.06 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.14 [-] Show Supplier Material materials with Relative density of 1.14 [-] | ASTM D 792 | |
Water absorption | 23.0 °C | 0.18 % Show Supplier Material materials with Water absorption of 0.18 % | ISO 62-1 | (23°C/saturated) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.7 GPa Show Supplier Material materials with Elastic modulus of 2.7 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 4.2 % Show Supplier Material materials with Elongation of 4.2 % | ISO 527 | break, 50 mm/min |
Flexural modulus | 23.0 °C | 2.7 GPa Show Supplier Material materials with Flexural modulus of 2.7 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 114 MPa Show Supplier Material materials with Flexural strength of 114 MPa | ISO 178 | yield, 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 9 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Impact strength, Izod notched | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m² | ISO 180/1A | 80*10*4, -30°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 36 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 36 J/m | ASTM D 256 |
Instrumented Impact, Total Energy | 23.0 °C | 18 J Show Supplier Material materials with Instrumented Impact, Total Energy of 18 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 56 MPa Show Supplier Material materials with Tensile strength of 56 MPa | ISO 527 | break, 50 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Ball Pressure Test | 125.0 | IEC 60695-10-2 | 125°C +/- 2°C | |||
Coefficient of thermal expansion | 23.0 °C | 7.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7.5E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 7.75E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7.75E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | ||||
Glow Wire Ignition Temperature | 800 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 800 °C | IEC 60695-2-13 | 2.0 mm | |||
Heat deflection temperature | 124 °C Show Supplier Material materials with Heat deflection temperature of 124 °C | ||||
Heat deflection temperature, 1.80 MPa | 124 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 124 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 110 °C Show Supplier Material materials with Relative temperature index, electrical of 110 °C | UL 746B | |||
Relative temperature index, mechanical impact | 105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | |||
Relative temperature index, mechanical strength | 110 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 110 °C | UL 746B | |||
Vicat softening temperature | 151 °C Show Supplier Material materials with Vicat softening temperature of 151 °C | ISO 306 | Rate B/120 | |||
Flammability | Glow Wire Ignitability Temperature, 1.0 mm: 825°C IEC 60695-2-13 <br> UL Recognized, 94-5VA Flame Class Rating: ≥2.5mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.75mm UL 94 <br> Glow Wire Flammability Index, 1.0 mm: 960°C IEC 60695-2-12 <br> UV-light, water exposure/immersion: F1- UL 746C <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103728770- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=103728771- - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Supplier Material materials with Comparative tracking index of 600 V | IEC 60112 | |
Dielectric constant, 60Hz | 23.0 °C | 2.7 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 2.7 [-] | IEC 60250 | 50/60 Hz |
Dielectric strength | 23.0 °C | 27 kV/mm Show Supplier Material materials with Dielectric strength of 27 kV/mm | IEC 60243-1 | in oil, 1.6 mm |
Dissipation factor, 1MHz | 23.0 °C | 2.9E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 2.9E-3 [-] | IEC 60250 |
High Amp Arc Ignition | 23.0 °C | 0.75 mm Show Supplier Material materials with High Amp Arc Ignition of 0.75 mm | ≥, UL 746A | PLC 3 |
Hot-Wire Ignition | 23.0 °C | 0.75 mm Show Supplier Material materials with Hot-Wire Ignition of 0.75 mm | ≥, UL 746A | PLC 2 |
Volume resistivity | 23.0 °C | 2.50E+16 - 4.20E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 2.50E+16 - 4.20E+16 Ω·cm | IEC 60093 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 13.5 g/10min Show Supplier Material materials with Melt mass-flow rate of 13.5 g/10min | ASTM D 1238 | 280°C/5.0 kgf | |
Melt volume-flow rate | 11 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 11 cm³/10min | ISO 1133 | MVR at 280°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage of 0.5 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Washing Machine, Pump, Freezer, Furnace/Heater, Electronic Components, Enclosures, Energy Management, Enclosure/Housing/Cover, Dishwasher, Displays, Cooking Range, Circuit Protection | |
Availability | Europe,Asia,Americas | |
Processing methods | Melt Temperature: 300 to 320.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |