General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.06 g/cm³ Show Supplier Material materials with Density of 1.06 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 0.5 % Show Supplier Material materials with Elongation of 0.5 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 12.3 GPa Show Supplier Material materials with Flexural modulus of 12.3 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 58 MPa Show Supplier Material materials with Flexural strength of 58 MPa | ISO 178 |
Impact strength, Izod notched | 23.0 °C | 4 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 4 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 58 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 58 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 82 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 82 J/m | ASTM D 4812 | 23°C |
Tensile strength | 23.0 °C | 55 MPa Show Supplier Material materials with Tensile strength of 55 MPa | ISO 527 | break, 5 mm/min |
Technological properties
Property | ||
---|---|---|
Application areas | Personal Computing | |
Availability | Asia,Americas | |
Processing methods | Melt Temperature: 225 to 250.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |