General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.18 g/cm³ Show Supplier Material materials with Density of 1.18 g/cm³ | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.43 % Show Supplier Material materials with Moisture absorption of 0.43 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.19 [-] Show Supplier Material materials with Relative density of 1.19 [-] | ASTM D 792 | |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.3 GPa Show Supplier Material materials with Elastic modulus of 2.3 GPa | ISO 527 | 1 mm/min | ||
Elongation | 23.0 °C | 46.7 % Show Supplier Material materials with Elongation of 46.7 % | ISO 527 | break | ||
Flexural modulus | 23.0 °C | 2.3 GPa Show Supplier Material materials with Flexural modulus of 2.3 GPa | ISO 178 | 2 mm/min | ||
Flexural strength | 23.0 °C | 93 MPa Show Supplier Material materials with Flexural strength of 93 MPa | ISO 178 | break, 2 mm/min | ||
Hardness, Rockwell L | 23.0 °C | 92.2 [-] Show Supplier Material materials with Hardness, Rockwell L of 92.2 [-] | ASTM D 785 | ||
Impact strength, Charpy notched | 23.0 °C | 12.9 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 12.9 kJ/m² | ISO 179/2C | -30°C | ||
Impact strength, Izod notched | 23.0 °C | 51.3 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 51.3 kJ/m² | ISO 180/1A | 80*10*4, 23°C | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 753 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 753 J/m | ASTM D 256 | ||
Instrumented Impact, Total Energy | 23.0 °C | 62.5 J Show Supplier Material materials with Instrumented Impact, Total Energy of 62.5 J | ASTM D 3763 | 23°C | ||
Tensile strength | 23.0 °C | 47 MPa Show Supplier Material materials with Tensile strength of 47 MPa | ISO 527 | break | ||
Impact strength, Charpy unnotched | ISO 179/2C | 23°C | ||||
Impact strength, Izod unnotched | ISO 180/1U | unnotched 80*10*4, 23°C | ||||
Impact strength, Izod unnotched, ASTM | ASTM D 4812 | 23°C |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 6.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 6.5E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 6.6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6.6E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature | 103 - 112 °C Show Supplier Material materials with Heat deflection temperature of 103 - 112 °C | ||||
Heat deflection temperature, 0.45 MPa | 112 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 112 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 103 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 103 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Vicat softening temperature | 119 °C Show Supplier Material materials with Vicat softening temperature of 119 °C | ISO 306 | Rate B/120 | |||
Flammability | UL Recognized, 94V-1 Flame Class Rating: ≥0.8mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.2mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103826700- - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 1GHz | 23.0 °C | 2.83 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 2.83 [-] | SABIC method | 1.1 GHz |
Dissipation factor, 1GHz | 23.0 °C | 6.1E-3 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 6.1E-3 [-] | SABIC method | |
Sheet resistivity, ROA | 23.0 °C | 1.00E+16 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+16 Ω | >, ASTM D 257 |
Volume resistivity | 23.0 °C | 1.00E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+16 Ω·cm | >, ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 20 g/10min Show Supplier Material materials with Melt mass-flow rate of 20 g/10min | ASTM D 1238 | 300°C/1.2 kgf | |
Shrinkage | 23.0 °C | 0.6 % Show Supplier Material materials with Shrinkage of 0.6 % | ASTM D 955 | 24 hrs |
Shrinkage, transverse | 23.0 °C | 0.62 % Show Supplier Material materials with Shrinkage, transverse of 0.62 % | ASTM D 955 | 24 hrs |
Technological properties
Property | ||
---|---|---|
Application areas | Wiring Devices, Wireless Communications, Monitoring and Imaging, Power Manangement, Industrial Material Handling, Electronics, Enclosures, Electronic Components | |
Availability | Asia | |
Processing methods | Drying Temperature: 100°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |