NORYL GTX™ 951W resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade exhibits high heat resistance, excellent chemical resistance, high melt flow, and added mold release. NORYL GTX951W resin was designed for automotive under-the-hood applications such as power distribution boxes, relay boxes, and junction boxes.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Relative density

23.0 °C

1.1 [-]

Show Supplier Material materials with Relative density of 1.1 [-]

ASTM D 792

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

51 %

Show Supplier Material materials with Elongation of 51 %

ISO 527 | break, 50 mm/min

Flexural modulus

23.0 °C

2.4 GPa

Show Supplier Material materials with Flexural modulus of 2.4 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

98 MPa

Show Supplier Material materials with Flexural strength of 98 MPa

ISO 178 | break, 2 mm/min

Impact strength, Izod notched

23.0 °C

8 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 8 kJ/m²

ISO 180/4A | notched 63.5*12.7*3.2, -30°C

Impact strength, Izod notched, ASTM

23.0 °C

211 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 211 J/m

ASTM D 256

Tensile strength

23.0 °C

66 MPa

Show Supplier Material materials with Tensile strength of 66 MPa

ISO 527 | yield, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.67E-4 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.67E-4 1/K

ASTM E 831 | 60°C to 138°C

Coefficient of thermal expansion, transverse

23.0 °C

1.53E-4 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 1.53E-4 1/K

ASTM E 831 | 60°C to 138°C

Heat deflection temperature

181 °C

Show Supplier Material materials with Heat deflection temperature of 181 °C

Heat deflection temperature, 0.45 MPa

181 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 181 °C

ISO 75/Be | Edgew 120*10*4 sp=100mm

Electrical

PropertyTemperatureValueComment

Dielectric strength

23.0 °C

22.4 kV/mm

Show Supplier Material materials with Dielectric strength of 22.4 kV/mm

ASTM D 149 | in oil, 1.6 mm

Dissipation factor, 1MHz

23.0 °C

0.02 [-]

Show Supplier Material materials with Dissipation factor, 1MHz of 0.02 [-]

ASTM D 150

Rheological Properties

PropertyValueComment

Melt mass-flow rate

65 g/10min

Show Supplier Material materials with Melt mass-flow rate of 65 g/10min

ASTM D 1238 | 280°C/5.0 kgf

Technological properties

Property
Application areas

Auto Electrical, Circuit Protection, Auto Aftermarket, Electronic Components, Recreational Vehicle

Availability

Europe,Asia,Americas

Processing methods

Shot to Cylinder Size: 30 to 50.0%
Front - Zone 3 Temperature: 265 to 295.0°C
Nozzle Temperature: 270 to 295.0°C
Back Pressure: 0.3 to 1.4MPa
Middle - Zone 2 Temperature: 260 to 295.0°C
Melt Temperature: 270 to 295.0°C
Drying Time (Cumulative): 8hrs
Rear - Zone 1 Temperature: 255 to 295.0°C
Vent Depth: 0.013 to 0.038mm
Minimum Moisture Content: 0.02%
Mold Temperature: 65 to 95.0°C
Maximum Moisture Content: 0.07%
Drying Time: 3 to 4.0hrs
Drying Temperature: 95 to 105.0°C
Screw Speed: 20 to 100.0rpm

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.