General
Property | Temperature | Value | Comment |
---|---|---|---|
Relative density | 23.0 °C | 1.35 [-] Show Supplier Material materials with Relative density of 1.35 [-] | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 5.2 GPa Show Supplier Material materials with Elastic modulus of 5.2 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 3 % Show Supplier Material materials with Elongation of 3 % | ASTM D 638 | yld, Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 5.2 GPa Show Supplier Material materials with Flexural modulus of 5.2 GPa | ASTM D 790 | 2.6 mm/min, 100 mm span |
Flexural strength | 23.0 °C | 193 MPa Show Supplier Material materials with Flexural strength of 193 MPa | ASTM D 790 | brk, 2.6 mm/min, 100 mm span |
Impact strength, Izod notched | 23.0 °C | 69 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 69 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 69 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 69 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 534 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 534 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 10 J Show Supplier Material materials with Instrumented Impact, Total Energy of 10 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 119 MPa Show Supplier Material materials with Tensile strength of 119 MPa | ASTM D 638 | yld, Type I, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 3.6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3.6E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 8.1E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 8.1E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature | 205 - 212 °C Show Supplier Material materials with Heat deflection temperature of 205 - 212 °C | ||||
Heat deflection temperature, 0.45 MPa | 212 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 212 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 205 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 205 °C | ASTM D 648 | 3.2mm, unannealed | |||
Relative temperature index, electrical | 155 °C Show Supplier Material materials with Relative temperature index, electrical of 155 °C | UL 746B | |||
Relative temperature index, mechanical impact | 155 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 155 °C | UL 746B | |||
Relative temperature index, mechanical strength | 155 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 155 °C | UL 746B | |||
Vicat softening temperature | 210 °C Show Supplier Material materials with Vicat softening temperature of 210 °C | ASTM D 1525 | Rate B/50 | |||
Flammability | UL Recognized, 94V-0 Flame Class Rating: ≥0.4mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221094- - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 4 V Show Supplier Material materials with Comparative tracking index of 4 V | UL 746A | (UL) {PLC} |
High Amp Arc Ignition | 23.0 °C | 0.4 mm Show Supplier Material materials with High Amp Arc Ignition of 0.4 mm | ≥, UL 746A | PLC 3 |
High Volt Arc Track Rate | 23.0 °C | 3 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 3 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 3 mm Show Supplier Material materials with Hot-Wire Ignition of 3 mm | ≥, UL 746A | PLC 1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 19 g/10min Show Supplier Material materials with Melt mass-flow rate of 19 g/10min | ASTM D 1238 | 337°C/6.6 kgf | |
Shrinkage | 23.0 °C | 0.7 % Show Supplier Material materials with Shrinkage of 0.7 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.6 % Show Supplier Material materials with Shrinkage, transverse of 0.6 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Electronic Components, Data Management, Data Transfer, Wireless Communications, LED Lighting | |
Availability | Asia,Americas | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |