LNP™ THERMOCOMP™ Compound UX08319

Want to keep this datasheet? Save it now in your required format

Description

LNP THERMOCOMP UX08319 is PPA base glass fiber filled compounds, good for LDS (Laser direct structuring)application. Additional feature is high heat. ...

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	2.14 g/cm³ Show Supplier Material materials with Density of 2.14 g/cm³	ASTM D 792

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	13.8 GPa Show Supplier Material materials with Elastic modulus of 13.8 GPa	ASTM D 638 \| 5 mm/min
Elongation	23.0 °C	1.4 % Show Supplier Material materials with Elongation of 1.4 %	ASTM D 638 \| brk, Type I, 5 mm/min
Flexural modulus	23.0 °C	11.5 GPa Show Supplier Material materials with Flexural modulus of 11.5 GPa	ASTM D 790 \| 1.3 mm/min, 50 mm span
Flexural strength	23.0 °C	185 MPa Show Supplier Material materials with Flexural strength of 185 MPa	ASTM D 790 \| yld, 1.3 mm/min, 50 mm span
Impact strength, Izod notched	23.0 °C	40 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 40 kJ/m²	ASTM D 256 \| notched, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	40 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 40 J/m	ASTM D 256
Tensile strength	23.0 °C	125 MPa Show Supplier Material materials with Tensile strength of 125 MPa	ASTM D 638 \| brk, Type I, 5 mm/min

Thermal

Property	Value	Comment
Heat deflection temperature	265 °C Show Supplier Material materials with Heat deflection temperature of 265 °C
Heat deflection temperature, 1.80 MPa	265 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 265 °C	ASTM D 648 \| 3.2mm, unannealed

Electrical

Property	Temperature	Value	Comment
Dielectric constant	23.0 °C	6.2 [-] Show Supplier Material materials with Dielectric constant of 6.2 [-]	SABIC method \| 1.9 GHz
Dissipation factor	23.0 °C	0.02 [-] Show Supplier Material materials with Dissipation factor of 0.02 [-]	SABIC method

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.33 % Show Supplier Material materials with Shrinkage of 0.33 %	SABIC method
Shrinkage, transverse	23.0 °C	0.35 % Show Supplier Material materials with Shrinkage, transverse of 0.35 %	SABIC method

Technological properties

Property
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 120 to 130.0°C Drying Time: 4 to 6.0hrs Melt Temperature: 315 to 330.0°C Front - Zone 3 Temperature: 300 to 330.0°C Middle - Zone 2 Temperature: 310 to 330.0°C Rear - Zone 1 Temperature: 300 to 320.0°C Mold Temperature: 140 to 165.0°C Back Pressure: 20 to 40.0MPa Screw Speed: 30 to 70.0rpm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.