General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.19 g/cm³ Show Supplier Material materials with Density of 1.19 g/cm³ | ISO 1183 |
Relative density | 23.0 °C | 1.19 [-] Show Supplier Material materials with Relative density of 1.19 [-] | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.1 GPa Show Supplier Material materials with Elastic modulus of 2.1 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 106 % Show Supplier Material materials with Elongation of 106 % | ISO 527 | break, 50 mm/min |
Flexural modulus | 23.0 °C | 2.2 GPa Show Supplier Material materials with Flexural modulus of 2.2 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 86 MPa Show Supplier Material materials with Flexural strength of 86 MPa | ISO 178 | yield, 2 mm/min |
Hardness, Rockwell L | 23.0 °C | 83 [-] Show Supplier Material materials with Hardness, Rockwell L of 83 [-] | ASTM D 785 |
Hardness, Rockwell R | 23.0 °C | 117 [-] Show Supplier Material materials with Hardness, Rockwell R of 117 [-] | ASTM D 785 |
Impact strength, Charpy notched | 23.0 °C | 29 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 29 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, -30°C |
Impact strength, Izod notched | 23.0 °C | 46 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 46 kJ/m² | ISO 180/1A | notched 80*10*3, -30°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 660 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 660 J/m | ASTM D 256 | notched, -30°C |
Instrumented Impact, Total Energy | 23.0 °C | 67 J Show Supplier Material materials with Instrumented Impact, Total Energy of 67 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 57 MPa Show Supplier Material materials with Tensile strength of 57 MPa | ISO 527 | yield, 50 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 7.42E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7.42E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 7.64E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7.64E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Heat deflection temperature | 117 - 131 °C Show Supplier Material materials with Heat deflection temperature of 117 - 131 °C | ||||
Heat deflection temperature, 0.45 MPa | 131 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 131 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |||
Heat deflection temperature, 1.80 MPa | 117 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 117 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |||
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Vicat softening temperature | 138 °C Show Supplier Material materials with Vicat softening temperature of 138 °C | ISO 306 | Rate B/120 | |||
Flammability | Glow Wire Flammability Index 960°C, passes at: 1mm IEC 60695-2-12 <br> Glow Wire Flammability Index 960°C, passes at: 1mm IEC 60695-2-12 <br> UL Recognized, 94-5VB Flame Class Rating: ≥1.5mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.5mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.5mm UL 94 <br> UL Recognized, 94-5VA Flame Class Rating: ≥3.1mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥1mm UL 94 <br> UL Recognized, 94V-1 Flame Class Rating: ≥0.8mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=102896543- - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 1GHz | 23.0 °C | 2.78 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 2.78 [-] | ASTM ES 7-83 | 1.1 GHz |
Dissipation factor, 1GHz | 23.0 °C | 6E-3 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 6E-3 [-] | ASTM ES 7-83 | 1.1 GHz |
Sheet resistivity, ROA | 23.0 °C | 1.00E+16 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+16 Ω | >, ASTM D 257 |
Volume resistivity | 23.0 °C | 1.00E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+16 Ω·cm | >, ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 11.5 g/10min Show Supplier Material materials with Melt mass-flow rate of 11.5 g/10min | ASTM D 1238 | 300°C/1.2 kgf | |
Melt volume-flow rate | 10 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 10 cm³/10min | ISO 1133 | MVR at 300°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.4 % Show Supplier Material materials with Shrinkage of 0.4 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.4 % Show Supplier Material materials with Shrinkage, transverse of 0.4 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Fast Charger, Mobile Phone, Drone, Battery Pack, Power Manangement, Scooter/Moped, Wireless Communications | |
Availability | Europe,Asia,Americas | |
Processing methods | Front - Zone 3 Temperature: 295 to 315.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |