LNP™ COLORCOMP™ Compound DX98550H

Want to keep this datasheet? Save it now in your required format

Description

LNP COLORCOMP DX98550H is an unfilled Polycarbonate resin. Added features of this grade are: Low Extractable, Healthcare.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Healthcare

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Relative density	23.0 °C	1.2 [-] Show Supplier Material materials with Relative density of 1.2 [-]	ASTM D 792

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.4 GPa Show Supplier Material materials with Elastic modulus of 2.4 GPa	ASTM D 638 \| 5 mm/min
Elongation	23.0 °C	120 % Show Supplier Material materials with Elongation of 120 %	ASTM D 638 \| brk, Type I, 5 mm/min
Flexural modulus	23.0 °C	2.3 GPa Show Supplier Material materials with Flexural modulus of 2.3 GPa	ASTM D 790 \| 1.3 mm/min, 50 mm span
Flexural strength	23.0 °C	86 MPa Show Supplier Material materials with Flexural strength of 86 MPa	ASTM D 790
Tensile strength	23.0 °C	60 MPa Show Supplier Material materials with Tensile strength of 60 MPa	ASTM D 638 \| brk, Type I, 5 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	3.3E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3.3E-5 1/K	ASTM E 831 \| -40°C to 40°C
Coefficient of thermal expansion, transverse	23.0 °C	3.3E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 3.3E-5 1/K	ASTM E 831 \| -40°C to 40°C
Relative temperature index, electrical		125 °C Show Supplier Material materials with Relative temperature index, electrical of 125 °C	UL 746B
Relative temperature index, mechanical impact		115 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 115 °C	UL 746B
Relative temperature index, mechanical strength		125 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 125 °C	UL 746B
Flammability	UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101283826- - <br> UL Recognized, 94V-2 Flame Class Rating: ≥1.5mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥1.5mm UL 94 <br> UL Recognized, 94HB Flame Class Rating: ≥2.5mm UL 94

Electrical

Property	Temperature	Value	Comment
Comparative tracking index	23.0 °C	4 V Show Supplier Material materials with Comparative tracking index of 4 V	UL 746A \| (UL) {PLC}
Dissipation factor, 1MHz	23.0 °C	0.01 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.01 [-]	ASTM D 150 \|
High Amp Arc Ignition	23.0 °C	1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm	≥, UL 746A \| PLC 3
High Volt Arc Track Rate	23.0 °C	2 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 2 PLC Code	UL 746A \| (PLC)
Hot-Wire Ignition	23.0 °C	1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm	≥, UL 746A \| PLC 3
Sheet resistivity, ROA	23.0 °C	1.00E+16 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+16 Ω	ASTM D 257
Volume resistivity	23.0 °C	1.00E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+16 Ω·cm	ASTM D 257

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.6 % Show Supplier Material materials with Shrinkage of 0.6 %	ASTM D 955 \| 24 hrs
Shrinkage, transverse	23.0 °C	0.6 % Show Supplier Material materials with Shrinkage, transverse of 0.6 %	ASTM D 955 \| 24 hrs

Technological properties

Property
Application areas	Surgical Devices, Pharmaceutical Packaging & Drug Delivery, Lab Ware and Clinical Diagnostics
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 120°C Drying Time: 4hrs Maximum Moisture Content: 0.02% Melt Temperature: 300 to 315.0°C Front - Zone 3 Temperature: 310 to 320.0°C Middle - Zone 2 Temperature: 305 to 315.0°C Rear - Zone 1 Temperature: 295 to 305.0°C Mold Temperature: 80 to 110.0°C Back Pressure: 0.2 to 0.3MPa Screw Speed: 30 to 60.0rpm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.