General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.33 g/cm³ Show Supplier Material materials with Density of 1.33 g/cm³ | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.1 % Show Supplier Material materials with Moisture absorption of 0.1 % | ASTM D 570 | (23°C/50% RH/24 hrs) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 16.6 GPa Show Supplier Material materials with Elastic modulus of 16.6 GPa | ASTM D 638 | 50 mm/min |
Elongation | 23.0 °C | 2.4 % Show Supplier Material materials with Elongation of 2.4 % | ASTM D 638 | break |
Flexural modulus | 23.0 °C | 15.5 GPa Show Supplier Material materials with Flexural modulus of 15.5 GPa | ASTM D 790 |
Flexural strength | 23.0 °C | 206 MPa Show Supplier Material materials with Flexural strength of 206 MPa | ASTM D 790 |
Impact strength, Izod notched | 23.0 °C | 58 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 58 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 58 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 58 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 480 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 480 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 11 J Show Supplier Material materials with Instrumented Impact, at Peak of 11 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 130 MPa Show Supplier Material materials with Tensile strength of 130 MPa | ASTM D 638 | yield |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.62E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.62E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 4.14E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 4.14E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature | 140 °C Show Supplier Material materials with Heat deflection temperature of 140 °C | ||||
Heat deflection temperature, 1.80 MPa | 140 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 140 °C | ASTM D 648 | 3.2mm, unannealed | |||
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101282789- - <br> UL Recognized, 94V-2 Flame Class Rating: 1.5mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: 1.5mm UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 100 - 1000000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 100 - 1000000 Ω | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Shrinkage, transverse | 23.0 °C | 0.3 % Show Supplier Material materials with Shrinkage, transverse of 0.3 % | ASTM D 955 | 24 hrs |
Technological properties
Property | ||
---|---|---|
Application areas | Enclosure/Housing/Cover, Data Management | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |