General
Property | Temperature | Value | Comment |
---|---|---|---|
Relative density | 23.0 °C | 1.31 [-] Show Supplier Material materials with Relative density of 1.31 [-] | ASTM D 792 |
Specific volume | 23.0 °C | 0.76 cm³/g Show Supplier Material materials with Specific volume of 0.76 cm³/g | ASTM D 792 |
Water absorption | 23.0 °C | 0.08 % Show Supplier Material materials with Water absorption of 0.08 % | ASTM D 570 | (23°C/24hrs) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 200 % Show Supplier Material materials with Elongation of 200 % | ASTM D 638 | brk, Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 2.3 GPa Show Supplier Material materials with Flexural modulus of 2.3 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Flexural strength | 23.0 °C | 82 MPa Show Supplier Material materials with Flexural strength of 82 MPa | ASTM D 790 | yld, 1.3 mm/min, 50 mm span |
Gardner Impact | 23.0 °C | 40 J Show Supplier Material materials with Gardner Impact of 40 J | ASTM D 3029 | modified, 23°C |
Hardness, Rockwell R | 23.0 °C | 117 [-] Show Supplier Material materials with Hardness, Rockwell R of 117 [-] | ASTM D 785 |
Impact strength, Izod notched | 23.0 °C | 53 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 53 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 53 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 53 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1602 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 1602 J/m | ASTM D 4812 | 23°C |
Tensile strength | 23.0 °C | 51 MPa Show Supplier Material materials with Tensile strength of 51 MPa | ASTM D 638 | brk, Type I, 50 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.39E-4 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.39E-4 1/K | ASTM E 831 | 60°C to 138°C | ||
Heat deflection temperature | 54 - 154 °C Show Supplier Material materials with Heat deflection temperature of 54 - 154 °C | ||||
Heat deflection temperature, 0.45 MPa | 154 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 154 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 54 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 54 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Relative temperature index, electrical | 120 °C Show Supplier Material materials with Relative temperature index, electrical of 120 °C | UL 746B | |||
Relative temperature index, mechanical impact | 120 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 120 °C | UL 746B | |||
Relative temperature index, mechanical strength | 140 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | |||
Flammability | UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103938350- - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 0 V Show Supplier Material materials with Comparative tracking index of 0 V | UL 746A | (UL) {PLC} |
Dielectric constant, 100Hz | 23.0 °C | 3.3 [-] Show Supplier Material materials with Dielectric constant, 100Hz of 3.3 [-] | ASTM D 150 |
Dielectric constant, 1MHz | 23.0 °C | 3.1 [-] Show Supplier Material materials with Dielectric constant, 1MHz of 3.1 [-] | ASTM D 150 |
Dielectric strength | 23.0 °C | 15.7 kV/mm Show Supplier Material materials with Dielectric strength of 15.7 kV/mm | ASTM D 149 | in oil, 3.2 mm |
Dissipation factor, 100Hz | 23.0 °C | 2E-3 [-] Show Supplier Material materials with Dissipation factor, 100Hz of 2E-3 [-] | ASTM D 150 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.02 [-] | ASTM D 150 |
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | ≥, UL 746A | PLC 0 |
High Volt Arc Track Rate | 23.0 °C | 1 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 1 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 6 mm Show Supplier Material materials with Hot-Wire Ignition of 6 mm | ≥, UL 746A | PLC 2 |
Volume resistivity | 23.0 °C | 4.00E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 4.00E+16 Ω·cm | >, ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt viscosity | 23.0 °C | 600 Pa·s Show Supplier Material materials with Melt viscosity of 600 Pa·s | SABIC method |
Shrinkage | 23.0 °C | 1.5 % Show Supplier Material materials with Shrinkage of 1.5 % | SABIC method | 2.3-4.6 mm |
Shrinkage, transverse | 23.0 °C | 1.6 % Show Supplier Material materials with Shrinkage, transverse of 1.6 % | SABIC method | 2.3-4.6 mm |
Technological properties
Property | ||
---|---|---|
Availability | Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |