LNP™ COLORCOMP™ Compound D10008PR

Want to keep this datasheet? Save it now in your required format

Description

COLORCOMP D10008PR is a compound based on Polycarbonate resin. Added features include: High Flow, Mold Release. For use in thin wall lighting lenses, data storage components and safety eyewear lenses.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Relative density	23.0 °C	1.2 [-] Show Supplier Material materials with Relative density of 1.2 [-]	ASTM D 792

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	120 % Show Supplier Material materials with Elongation of 120 %	ASTM D 638 \| brk, Type I, 50 mm/min
Flexural modulus	23.0 °C	2.3 GPa Show Supplier Material materials with Flexural modulus of 2.3 GPa	ASTM D 790 \| 1.3 mm/min, 50 mm span
Flexural strength	23.0 °C	93 MPa Show Supplier Material materials with Flexural strength of 93 MPa	ASTM D 790 \| yld, 1.3 mm/min, 50 mm span
Impact strength, Izod notched	23.0 °C	640 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 640 kJ/m²	ASTM D 256 \| notched, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	640 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 640 J/m	ASTM D 256 \| notched, 23°C
Instrumented Impact, at Peak	23.0 °C	54 J Show Supplier Material materials with Instrumented Impact, at Peak of 54 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	65 MPa Show Supplier Material materials with Tensile strength of 65 MPa	ASTM D 638 \| brk, Type I, 50 mm/min

Thermal

Property	Value	Comment
Heat deflection temperature	126 °C Show Supplier Material materials with Heat deflection temperature of 126 °C
Heat deflection temperature, 1.80 MPa	126 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 126 °C	ASTM D 648 \| 3.2mm, unannealed
Relative temperature index, electrical	130 °C Show Supplier Material materials with Relative temperature index, electrical of 130 °C	UL 746B
Relative temperature index, mechanical impact	130 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 130 °C	UL 746B
Relative temperature index, mechanical strength	130 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 130 °C	UL 746B
Flammability	UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103956751- - <br> UL Recognized, 94V-2 Flame Class Rating: ≥1.1mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥1.1mm UL 94

Electrical

Property	Temperature	Value	Comment
Comparative tracking index	23.0 °C	2 V Show Supplier Material materials with Comparative tracking index of 2 V	UL 746A \| (UL) {PLC}
High Amp Arc Ignition	23.0 °C	1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm	≥, UL 746A \| PLC 0
High Volt Arc Track Rate	23.0 °C	2 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 2 PLC Code	UL 746A \| (PLC)
Hot-Wire Ignition	23.0 °C	1.1 mm Show Supplier Material materials with Hot-Wire Ignition of 1.1 mm	≥, UL 746A \| PLC 3

Optical

Property	Value	Comment
Haze	1 % Show Supplier Material materials with Haze of 1 %	ASTM D 1003 \| 2.54 mm
Transmission	88 % Show Supplier Material materials with Transmission of 88 %	ASTM D 1003 \| 2.54 mm

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		25 g/10min Show Supplier Material materials with Melt mass-flow rate of 25 g/10min	ASTM D 1238 \| 300°C/1.2 kgf
Shrinkage	23.0 °C	0.5 % Show Supplier Material materials with Shrinkage of 0.5 %	SABIC method \| 3.2 mm

Technological properties

Property
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 120°C Drying Time: 3 to 4.0hrs Drying Time (Cumulative): 48hrs Maximum Moisture Content: 0.02% Melt Temperature: 270 to 295.0°C Nozzle Temperature: 265 to 290.0°C Front - Zone 3 Temperature: 270 to 295.0°C Middle - Zone 2 Temperature: 260 to 280.0°C Rear - Zone 1 Temperature: 250 to 270.0°C Mold Temperature: 70 to 95.0°C Back Pressure: 0.3 to 0.7MPa Screw Speed: 40 to 70.0rpm Shot to Cylinder Size: 40 to 60.0% Vent Depth: 0.025 to 0.076mm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.