General
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of friction | 0.17 - 0.28 [-] Show Supplier Material materials with Coefficient of friction of 0.17 - 0.28 [-] | ||
Coefficient of friction, kinetic | 0.28 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.28 [-] | ASTM D 3702 Modified: Manual | |
Coefficient of friction, static | 0.17 [-] Show Supplier Material materials with Coefficient of friction, static of 0.17 [-] | ASTM D 3702 Modified: Manual | |
Density | 23.0 °C | 1.25 g/cm³ Show Supplier Material materials with Density of 1.25 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.2 % Show Supplier Material materials with Moisture absorption of 0.2 % | ISO 62 | (23°C / 50% RH) |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.5 GPa Show Supplier Material materials with Elastic modulus of 2.5 GPa | ISO 527 | 1 mm/min | ||
Elongation | 23.0 °C | 23.1 % Show Supplier Material materials with Elongation of 23.1 % | ISO 527 | break | ||
Flexural modulus | 23.0 °C | 2.1 GPa Show Supplier Material materials with Flexural modulus of 2.1 GPa | ISO 178 | ||
Flexural strength | 23.0 °C | 85 MPa Show Supplier Material materials with Flexural strength of 85 MPa | ISO 178 | ||
Impact strength, Izod notched | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 10 kJ/m² | ISO 180/1A | 80*10*4, 23°C | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 106 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 106 J/m | ASTM D 256 | notched, 23°C | ||
Instrumented Impact, at Peak | 23.0 °C | 34 J Show Supplier Material materials with Instrumented Impact, at Peak of 34 J | ASTM D 3763 | 23°C | ||
Tensile strength | 23.0 °C | 43 MPa Show Supplier Material materials with Tensile strength of 43 MPa | ISO 527 | break | ||
Impact strength, Izod unnotched | ISO 180/1U | unnotched 80*10*4, 23°C | ||||
Impact strength, Izod unnotched, ASTM | ASTM D 4812 | 23°C |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 6.67E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 6.67E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 7.33E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 7.33E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Heat deflection temperature | 123 °C Show Supplier Material materials with Heat deflection temperature of 123 °C | ||
Heat deflection temperature, 1.80 MPa | 123 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 123 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt volume-flow rate | 13.5 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 13.5 cm³/10min | ASTM D 1238 | MVR at 300°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.7 % Show Supplier Material materials with Shrinkage of 0.7 % | ISO 294 | 24 hrs |
Shrinkage, transverse | 23.0 °C | 1 % Show Supplier Material materials with Shrinkage, transverse of 1 % | ISO 294 | 24 hrs |
Technological properties
Property | ||
---|---|---|
Application areas | Wireless Communications, Personal Computing, Small Appliance, Enclosures | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |