Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.25 g/cm³ Show Supplier Material materials with Density of 1.25 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.04 % Show Supplier Material materials with Moisture absorption of 0.04 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.26 [-] Show Supplier Material materials with Relative density of 1.26 [-] | ASTM D 792 |
Water absorption | 23.0 °C | 0.13 % Show Supplier Material materials with Water absorption of 0.13 % | ISO 62-1 | (23°C/saturated) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 3.7 GPa Show Supplier Material materials with Elastic modulus of 3.7 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 9 % Show Supplier Material materials with Elongation of 9 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 3.3 GPa Show Supplier Material materials with Flexural modulus of 3.3 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Flexural strength | 23.0 °C | 95 MPa Show Supplier Material materials with Flexural strength of 95 MPa | ASTM D 790 | yld, 1.3 mm/min, 50 mm span |
Impact strength, Charpy notched | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 9 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, -30°C |
Impact strength, Charpy unnotched | 23.0 °C | 102 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 102 kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, -30°C |
Impact strength, Izod notched | 23.0 °C | 20 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 20 kJ/m² | ISO 180/1A | 80*10*3, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 230 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 230 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched | 23.0 °C | 68 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 68 kJ/m² | ISO 180/1U | unnotched 80*10*3, -30°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1700 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 1700 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 36 J Show Supplier Material materials with Instrumented Impact, Total Energy of 36 J | ASTM D 3763 | 23°C |
Tensile strength | 23.0 °C | 59 MPa Show Supplier Material materials with Tensile strength of 59 MPa | ISO 527 | yield, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Ball Pressure Test | nan | IEC 60695-10-2 | 125°C +/- 2°C | |||
Coefficient of thermal expansion | 23.0 °C | 3E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 8E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 8E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | ||||
Glow Wire Ignition Temperature | 900 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 900 °C | IEC 60695-2-13 | 3.0 mm | |||
Heat deflection temperature | 125 - 131 °C Show Supplier Material materials with Heat deflection temperature of 125 - 131 °C | ||||
Heat deflection temperature, 0.45 MPa | 131 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 131 °C | ASTM D 648 | 3.2 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 125 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 125 °C | ASTM D 648 | 3.2mm, unannealed | |||
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Vicat softening temperature | 135 °C Show Supplier Material materials with Vicat softening temperature of 135 °C | ISO 306 | Rate B/120 | |||
Flammability | UL Recognized, 94HB Flame Class Rating: ≥0.4mm UL 94 <br> Glow Wire Ignitability Temperature, 1.0 mm: 930°C IEC 60695-2-13 <br> Glow Wire Flammability Index, 1.0 mm: 930°C IEC 60695-2-12 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101177358- - |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 15 g/10min Show Supplier Material materials with Melt mass-flow rate of 15 g/10min | ASTM D 1238 | 300°C/1.2 kgf | |
Melt volume-flow rate | 14 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 14 cm³/10min | ISO 1133 | MVR at 300°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.2 % Show Supplier Material materials with Shrinkage of 0.2 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.4 % Show Supplier Material materials with Shrinkage, transverse of 0.4 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Wireless Communications, Wearables, Watch/Jewelry, Personal Computing, Photo/Video Camera, Enclosures, Electronics, EV Infrastructure | |
Availability | Europe,Asia,Americas | |
Processing methods | Middle - Zone 2 Temperature: 275 to 300.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |