LNP™ THERMOCOMP™ Compound DF008ERH

Want to keep this datasheet? Save it now in your required format

Description

LNP THERMOCOMP* DF008ERH is a compound based on Polycarbonate resin containing 40% Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Healthcare.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Healthcare

Medical Equipment

Surgical Instruments

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Moisture absorption	23.0 °C	0.12 % Show Supplier Material materials with Moisture absorption of 0.12 %	ISO 62 \| (23°C / 50% RH)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	11.2 GPa Show Supplier Material materials with Elastic modulus of 11.2 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	2.2 % Show Supplier Material materials with Elongation of 2.2 %	ISO 527 \| break
Flexural modulus	23.0 °C	11 GPa Show Supplier Material materials with Flexural modulus of 11 GPa	ISO 178
Flexural strength	23.0 °C	203 MPa Show Supplier Material materials with Flexural strength of 203 MPa	ISO 178
Impact strength, Izod notched	23.0 °C	11 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 11 kJ/m²	ISO 180/1A \| notched 80104, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	218 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 218 J/m	ASTM D 256 \| notched, 23°C
Impact strength, Izod unnotched	23.0 °C	53 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 53 kJ/m²	ISO 180/1U \| unnotched 80104, 23°C
Impact strength, Izod unnotched, ASTM	23.0 °C	806 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 806 J/m	ASTM D 4812 \| 23°C
Instrumented Impact, at Peak	23.0 °C	13 J Show Supplier Material materials with Instrumented Impact, at Peak of 13 J	ASTM D 3763 \| 23°C
Tensile strength	23.0 °C	136 MPa Show Supplier Material materials with Tensile strength of 136 MPa	ISO 527 \| break

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	3.26E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3.26E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Coefficient of thermal expansion, transverse	23.0 °C	3.51E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 3.51E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Heat deflection temperature		137 °C Show Supplier Material materials with Heat deflection temperature of 137 °C
Heat deflection temperature, 1.80 MPa		137 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 137 °C	ISO 75/Af \| Flatw 80104 sp=64mm

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.16 % Show Supplier Material materials with Shrinkage of 0.16 %	ISO 294 \| 24 hrs
Shrinkage, transverse	23.0 °C	0.35 % Show Supplier Material materials with Shrinkage, transverse of 0.35 %	ISO 294 \| 24 hrs

Technological properties

Property
Application areas	Surgical Devices
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 120°C Drying Time: 4hrs Maximum Moisture Content: 0.02% Melt Temperature: 305 to 325.0°C Front - Zone 3 Temperature: 320 to 330.0°C Middle - Zone 2 Temperature: 310 to 320.0°C Rear - Zone 1 Temperature: 295 to 305.0°C Mold Temperature: 80 to 110.0°C Back Pressure: 0.2 to 0.3MPa Screw Speed: 30 to 60.0rpm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.