General
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 8 - 10 % Show Supplier Material materials with Elongation of 8 - 10 % | SABIC - Japan Method | break |
Flexural modulus | 23.0 °C | 5.6 GPa Show Supplier Material materials with Flexural modulus of 5.6 GPa | ASTM D 790 |
Flexural strength | 23.0 °C | 142 MPa Show Supplier Material materials with Flexural strength of 142 MPa | ASTM D 790 |
Hardness, Rockwell R | 23.0 °C | 124 [-] Show Supplier Material materials with Hardness, Rockwell R of 124 [-] | ASTM D 785 |
Impact strength, Izod notched | 23.0 °C | 107 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 107 kJ/m² | ASTM D 256 | notched, 23°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 107 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 107 J/m | ASTM D 256 | notched, 23°C |
Tensile strength | 23.0 °C | 98 MPa Show Supplier Material materials with Tensile strength of 98 MPa | SABIC - Japan Method | yield |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.8E-5 - 4.5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.8E-5 - 4.5E-5 1/K | TMA | -30°C to 30°C | ||
Heat deflection temperature | 139 °C Show Supplier Material materials with Heat deflection temperature of 139 °C | ||||
Heat deflection temperature, 1.80 MPa | 139 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 139 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Relative temperature index, electrical | 65 °C Show Supplier Material materials with Relative temperature index, electrical of 65 °C | UL 746B | |||
Relative temperature index, mechanical impact | 65 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | |||
Relative temperature index, mechanical strength | 65 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | |||
Flammability | UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=237021- - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 3 V Show Supplier Material materials with Comparative tracking index of 3 V | UL 746A | (UL) {PLC} |
Dielectric constant, 60Hz | 23.0 °C | 2.86 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 2.86 [-] | ASTM D 150 | 50/60 Hz |
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | ≥, UL 746A | PLC 0 |
High Volt Arc Track Rate | 23.0 °C | 4 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | ≥, UL 746A | PLC 3 |
Sheet resistivity, ROA | 23.0 °C | 1.00E+16 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+16 Ω | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 11.1 g/10min Show Supplier Material materials with Melt mass-flow rate of 11.1 g/10min | ASTM D 1238 | 300°C/5.0 kgf | |
Shrinkage | 23.0 °C | 0.2 % Show Supplier Material materials with Shrinkage of 0.2 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Electronic Components, Electrical, Plumbing | |
Availability | Asia | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |